CHARACTERISTICS OF SHRINKAGE COMPENSATING EXPANSIVE CEMENT CONTAINING A PRE-HYDRATED HIGH-ALUMINA CEMENT-BASED EXPANSIVE ADDITIVE

被引：9
|
作者：
FU, Y [1 ]
XIE, P [1 ]
GU, P [1 ]
BEAUDOIN, JJ [1 ]
机构：
[1] NATL RES COUNCIL CANADA,INST RES CONSTRUCT,MAT LAB,OTTAWA K1A 0R6,ONTARIO,CANADA
来源：
CEMENT AND CONCRETE RESEARCH | 1994年 / 24卷 / 02期
基金：
加拿大自然科学与工程研究理事会;
关键词：
D O I：
10.1016/0008-8846(94)90052-3
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Research directed at developing a new composite expansive additive for use in producing shrinkage-compensating cement by addition to Portland cement is reported. Setting time, flow loss, free expansion, restrained expansion and compressive strength results were obtained for cement pastes and mortars containing different amounts of expansive additive. The effect of superplasticizer on the properties of fresh and hardened expansive cement mortar was also investigated. Results indicated that expansive cement with an appropriate amount of pre-hydrated high alumina cement based expansive additive passes all the requirements of relevant ASTM standards and is potentially of practical use.
引用
收藏
页码：267 / 276
页数：10
相关论文
共 50 条
  • [41] Effects of curing temperature and superabsorbent polymers on hydration of early-age cement paste containing a CaO-based expansive additive
    Haitao Zhao
    Kaidi Jiang
    Yunfei Di
    Wen Xu
    Wei Li
    Qian Tian
    Jiaping Liu
    Materials and Structures, 2019, 52
  • [42] Effects of curing temperature and superabsorbent polymers on hydration of early-age cement paste containing a CaO-based expansive additive
    Zhao, Haitao
    Jiang, Kaidi
    Di, Yunfei
    Xu, Wen
    Li, Wei
    Tian, Qian
    Liu, Jiaping
    MATERIALS AND STRUCTURES, 2019, 52 (06)
  • [43] A synergetic self-sealing model for cement-based composite using granular expansive agent and crystalline admixture
    Li, Desheng
    Lai, Yuanming
    Wen, Zhi
    Gao, Qiang
    Ding, Zhaowei
    Zheng, Hao
    Chen, Bing
    MATERIALS & DESIGN, 2024, 245
  • [44] Effects of calcination condition on expansion property of MgO-type expansive agent used in cement-based materials
    Mo, Liwu
    Deng, Min
    Tang, Mingshu
    CEMENT AND CONCRETE RESEARCH, 2010, 40 (03) : 437 - 446
  • [45] Mechanism underlying effects of CaO-MgO combined expansive agent on hydration kinetics of cement-based systems
    Chen, Zheng
    Zhao, Jie
    Wu, Changjie
    Chen, Ben
    Dai, Mingxuan
    JOURNAL OF SUSTAINABLE CEMENT-BASED MATERIALS, 2024, 13 (07) : 978 - 994
  • [46] Effect of an expansive agent on the interfacial bond and mechanical properties of carbon fibre-reinforced cement-based composites
    Dai, Jinghui
    Wang, Jun
    Xiao, Huigang
    MAGAZINE OF CONCRETE RESEARCH, 2023, 76 (09) : 455 - 467
  • [47] Crystal structure solution of hydrated high-alumina cement from X-ray powder diffraction data
    Guirado, F
    Galí, S
    Chinchón, S
    Rius, J
    ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 1998, 37 (1-2) : 72 - 75
  • [48] Autogenous shrinkage of high-performance cement-based carbon nanofiber composites
    Zhang, Yan
    Cheng, Yongfeng
    Zhang, Tingting
    Wang, Baomin
    Xiao, Hong
    MATERIALS EXPRESS, 2019, 9 (03) : 213 - 225
  • [49] Autogenous Shrinkage Property of High-Performance Graphenes Cement-Based Composites
    Liu, Fang
    Wang, Baomin
    Yuan, Xiaosa
    Wang, Yonggang
    Shen, Lin
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2020, 20 (02) : 828 - 839
  • [50] An overview on the effect of internal curing on shrinkage of high performance cement-based materials
    Liu, Jianhui
    Shi, Caijun
    Ma, Xianwei
    Khayat, Kamal H.
    Zhang, Jian
    Wang, Dehui
    CONSTRUCTION AND BUILDING MATERIALS, 2017, 146 : 702 - 712
12345