CHARACTERISTICS OF SHRINKAGE COMPENSATING EXPANSIVE CEMENT CONTAINING A PRE-HYDRATED HIGH-ALUMINA CEMENT-BASED EXPANSIVE ADDITIVE

被引：9
|
作者：
FU, Y [1 ]
XIE, P [1 ]
GU, P [1 ]
BEAUDOIN, JJ [1 ]
机构：
[1] NATL RES COUNCIL CANADA,INST RES CONSTRUCT,MAT LAB,OTTAWA K1A 0R6,ONTARIO,CANADA
来源：
CEMENT AND CONCRETE RESEARCH | 1994年 / 24卷 / 02期
基金：
加拿大自然科学与工程研究理事会;
关键词：
D O I：
10.1016/0008-8846(94)90052-3
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Research directed at developing a new composite expansive additive for use in producing shrinkage-compensating cement by addition to Portland cement is reported. Setting time, flow loss, free expansion, restrained expansion and compressive strength results were obtained for cement pastes and mortars containing different amounts of expansive additive. The effect of superplasticizer on the properties of fresh and hardened expansive cement mortar was also investigated. Results indicated that expansive cement with an appropriate amount of pre-hydrated high alumina cement based expansive additive passes all the requirements of relevant ASTM standards and is potentially of practical use.
引用
收藏
页码：267 / 276
页数：10
相关论文
共 50 条
  • [1] EFFECT OF CHEMICAL ADMIXTURES ON THE EXPANSION OF SHRINKAGE-COMPENSATING CEMENT CONTAINING A PRE-HYDRATED HIGH-ALUMINA CEMENT-BASED EXPANSIVE ADDITIVE
    FU, Y
    GU, P
    XIE, P
    BEAUDOIN, JJ
    CEMENT AND CONCRETE RESEARCH, 1995, 25 (01) : 29 - 38
  • [2] EXPANSION CHARACTERISTICS OF A COMPOUNDED-EXPANSIVE ADDITIVE AND PRE-HYDRATED HIGH-ALUMINA CEMENT-BASED EXPANSIVE ADDITIVE
    FU, Y
    DING, J
    BEAUDOIN, JJ
    CEMENT AND CONCRETE RESEARCH, 1995, 25 (06) : 1295 - 1304
  • [3] Expansive cement blend for use in shrinkage-compensating mortars
    Ribeiro, MSS
    MATERIALS AND STRUCTURES, 1998, 31 (210): : 400 - 404
  • [4] Expansive cement blend for use in shrinkage-compensating mortars
    Laboratorio Nacional de Engenharia, Civil, Lisbon, Portugal
    Mater Struct, 210 (400-404):
  • [5] BRECEM - A RAPID HARDENING CEMENT-BASED ON HIGH-ALUMINA CEMENT
    OSBORNE, GJ
    PROCEEDINGS OF THE INSTITUTION OF CIVIL ENGINEERS-STRUCTURES AND BUILDINGS, 1994, 104 (01) : 93 - 100
  • [6] Expansive cement blend for use in shrinkage-compensating mortars
    Maria Sofia Sousa Ribeiro
    Materials and Structures, 1998, 31 (6) : 400 - 404
  • [7] Effect of different calcium aluminate hydrates on ettringite formation and expansion of high alumina cement-based expansive cement pastes
    Fu, Y
    Ding, J
    Beaudoin, JJ
    CEMENT AND CONCRETE RESEARCH, 1996, 26 (03) : 417 - 426
  • [8] Effects of MgO-based expansive additive on compensating the shrinkage of cement paste under non-wet curing conditions
    Mo, L.
    Deng, M.
    Wang, A.
    CEMENT & CONCRETE COMPOSITES, 2012, 34 (03): : 377 - 383
  • [9] Chemical shrinkage and autogenous volume change of cement paste added with expansive additive
    Morioka, Minoru
    Hagiwara, Hirotoshi
    Sakai, Etsuo
    Daimon, Masaki
    Transactions of the Japan Concrete Institute, 1999, 21 : 107 - 114
  • [10] Shrinkage and cracking behavior of cement based materials containing undercalcined MgO-based expansive agent
    Zhang, Shouzhi
    Tian, Qian
    Yao, Ting
    Guo, Fei
    ARCHITECTURE, BUILDING MATERIALS AND ENGINEERING MANAGEMENT, PTS 1-4, 2013, 357-360 : 1148 - 1153
12345