INHIBITION OF HYDROGEN PERMEATION IN STEELS CORRODING IN SOUR FLUIDS

被引：13
|
作者：
MARTIN, RL
机构：
[1] Petrolite Corp, St. Louis, MO
来源：
CORROSION | 1993年 / 49卷 / 08期
关键词：
CORROSION FATIGUE; GAS PLANTS; HYDROGEN-INDUCED CRACKING; HYDROGEN PERMEATION; INHIBITION; OIL WELLS;
D O I：
10.5006/1.3316102
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion inhibitor effects of mobile and trapped hydrogen (H) in steels corroding in sour fluids were investigated. Field tests were conducted on corrosion fatigue, one of the ramifications of H in steel. H measurements were made on a sour gas separator vessel wall. An explanation for inhibition of H entry was proposed.
引用
收藏
页码：694 / 701
页数：8
相关论文
共 50 条
  • [31] Examination of Hydrogen Diffusivity in Carbon Steels Using a Newly Developed Hydrogen Permeation System
    M. Okayasu
    M. Sato
    Experimental Mechanics, 2021, 61 : 1443 - 1453
  • [32] HYDROGEN-INDUCED CRACKING OF LINE PIPE STEELS USED IN SOUR SERVICE
    REVIE, RW
    SASTRI, VS
    ELBOUJDAINI, M
    RAMSINGH, RR
    LAFRENIERE, Y
    CORROSION, 1993, 49 (07) : 531 - 535
  • [33] Modelling the combined effects of hydrogen traps and surface films on hydrogen permeation in ferritic steels
    Zhi, Huihui
    Yu, Haiyang
    Gao, Lei
    Zhang, Zhiliang
    Su, Yanjing
    ANTI-CORROSION METHODS AND MATERIALS, 2020, 67 (02) : 240 - 247
  • [34] Effect of Membrane Thickness on Hydrogen Permeation in Steels During Wet Hydrogen Sulfide Exposure
    Kittel, J.
    Ropital, F.
    Pellier, J.
    CORROSION, 2008, 64 (10) : 788 - 799
  • [35] METHODS OF TESTING CORRODING INFLUENCE OF CUTTING FLUIDS
    BULAT, A
    MECHANIK MIESIECZNIK NAUKOWO-TECHNICZNY, 1971, 44 (03): : 140 - &
  • [36] Stress corrosion cracking by anodic dissolution and hydrogen permeation in pipeline steels
    S. Di Liberto
    G. Gabetta
    Materials Science, 1997, 33 : 411 - 420
  • [37] Stress corrosion cracking by anodic dissolution and hydrogen permeation in pipeline steels
    Di Liberto, S
    Gabetta, G
    MATERIALS SCIENCE, 1997, 33 (04) : 411 - 420
  • [38] Effect of retained austenite on the hydrogen permeation behavior in high strength steels
    Tsubakino, H
    Harada, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1997, 83 (09): : 587 - 592
  • [39] Influence of plastic strain on the permeation of hydrogen in chromium-molybdenum steels
    Brass, AM
    Garet, M
    Etter, AL
    Vivet, S
    HYDROGEN EFFECTS ON MATERIAL BEHAVIOR AND CORROSION DEFORMATION INTERACTIONS, 2003, : 3 - 16
  • [40] INVESTIGATIONS ON THE INFLUENCE OF MICROSTRUCTURE OF STEELS ON STEADY-STATE HYDROGEN PERMEATION
    RIECKE, E
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1981, 32 (02): : 66 - 72
12345