EFFECT OF TI(C,N) ADDITION ON SINTERING BEHAVIOR AND PROPERTIES OF BINDER-MODIFIED WC-10CO CEMENTED CARBIDE

被引：7
|
作者：
BHAUMIK, SK
UPADHYAYA, GS
VAIDYA, ML
机构：
[1] Department of Materials and Metallurgical Engineering, Indian Institute of Technology, Kanpur
来源：
JOURNAL OF MATERIALS SCIENCE | 1994年 / 29卷 / 01期
关键词：
D O I：
10.1007/BF00356572
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present investigation the microstructure and mechanical properties of WC-10Co, WC-8.3Ti(C,N)-12Co, WC-8.3Ti(C,N)-6Co-6Ni and WC-7Ti(C,N)-2Mo2C-6Co-6Ni cemented carbides were studied. Introduction of Ti(C,N) in WC-10Co cemented carbide imposed sintering difficulties and hot isostatic pressing was required to obtain fully dense material. The modification of the binder cobalt with nickel and molybdenum did not noticeably affect the sintered microstructure. In general the mechanical properties of Ti(C,N)-containing cemented carbides were inferior to those of WC-10Co cemented carbide.
引用
收藏
页码：54 / 60
页数：7
相关论文
共 50 条
  • [21] Effects of Processing Parameters on the Microstructure and Mechanical Properties of Nanoscaled WC-10Co Cemented Carbide
    Wang, Yu
    Xiang, Fengming
    Yuan, Xiaobo
    Yang, Biaobiao
    Wang, Fenglin
    Li, Yunping
    MATERIALS, 2022, 15 (13)
  • [22] Effects of addition of ultrafine WC and fine WC/Coon microstructure and mechanical properties of WC-10Co cemented carbides
    Yu, Songbai
    Jiang, Haoli
    Min, Fanlu
    Zhang, Hailong
    Wang, Congxu
    Yao, Zhanhu
    Zhang, Jianfeng
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2023, 51 (07): : 136 - 145
  • [23] Powder Extrusion Molding of Nanocrystalline WC-10Co Composite Cemented Carbide
    史晓亮
    Journal of Wuhan University of Technology(Materials Science Edition), 2006, (01) : 46 - 48
  • [24] Powder extrusion molding of nanocrystalline WC-10Co composite cemented carbide
    State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China
    J Wuhan Univ Technol Mater Sci Ed, 2006, 1 (46-48):
  • [25] Powder extrusion molding of nanocrystalline WC-10Co composite cemented carbide
    Shi, XL
    Shao, GQ
    Duan, XL
    Yuan, RZ
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2006, 21 (01): : 46 - 48
  • [26] SINTERING BEHAVIOR OF A WC-CO CEMENTED CARBIDE (12 WC-PERCENT-CO) WITH BINDER PHASES OF DIFFERENT COMPOSITIONS
    EXNER, HE
    FREYTAG, J
    PETZOW, G
    WALTER, P
    PLANSEEBERICHTE FUR PULVERMETALLURGIE, 1978, 26 (02): : 90 - 104
  • [27] Effects of sintering method and Al2O3 content on microstructure and mechanical properties of WC-10Co cemented carbide
    Deng, Xiao-Chun
    Zhang, Guo-Hua
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 124
  • [28] EFFECT OF TIN ADDITION ON SINTERING BEHAVIOR AND MECHANICAL-PROPERTIES OF WC-10CO HARD METALS CONTAINING MO2C AND NI
    BHAUMIK, SK
    UPADHYAYA, GS
    VAIDYA, ML
    JOURNAL OF MATERIALS SCIENCE, 1992, 27 (07) : 1947 - 1959
  • [29] Influences of ball-milled time on properties and microstructure of ultrafine WC-10Co cemented carbide
    Shi, X. L.
    Shao, G. Q.
    Duan, X. L.
    NANOSCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2007, 121-123 : 1337 - 1340
  • [30] A TRANSMISSION ELECTRON-MICROSCOPY STUDY OF WC-10CO CEMENTED CARBIDES WITH MODIFIED HARD AND BINDER PHASES
    BHAUMIK, SK
    UPADHYAYA, GS
    VAIDYA, ML
    MATERIALS CHARACTERIZATION, 1992, 28 (03) : 241 - 249
12345