ON THE KINETICS OF HYDROLYSIS OF MAGNESIUM CLINKER TEMPERED AT TEMPERATURES ABOVE 1000-DEGREES-C

被引：0
|
作者：
UZUNOVA, I [1 ]
KOEV, K [1 ]
机构：
[1] HIGHER INST ECON,VARNA,BULGARIA
来源：
ENVIRONMENTAL TECHNOLOGY | 1990年 / 11卷 / 05期
关键词：
D O I：
10.1080/09593339009384883
中图分类号：
X [环境科学、安全科学];
学科分类号：
08 ; 0830 ;
摘要：
The degre of hydrolysis of MgO and its dependence on the hydrolitic process temperature, as well as on the tempering temperature are established. It is shown that even if tempered at about 1500°C MgO is not an inert material. Under the impact of some external factors‐temperature (40°C to 120°C) and water‐it hydrolyzes in different degree. It should be borne in mind that accidents are possible to occur with transport vehicle which are in contact with magnesium clinker and water. © 1990 Publications Division Selper Ltd.
引用
收藏
页码：437 / 442
页数：6
相关论文
共 50 条
  • [31] A SIMPLE METHOD FOR MAKING TRANSPARENT SILICA AT 1000-DEGREES-C
    CLEGG, WJ
    ALFORD, NM
    BIRCHALL, JD
    KENDALL, K
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1990, 200 : 225 - COLL
  • [32] CYCLIC FATIGUE OF SILICON-NITRIDE AT 1000-DEGREES-C
    BUSHBY, A
    GUIU, F
    KNOWLES, J
    REECE, MJ
    SILICON NITRIDE 93, 1994, 89-9 : 673 - 677
  • [33] MICROSTRUCTURE AND PHYSICOCHEMICAL STUDIES OF PURE AND ZINC-SUBSTITUTED LITHIUM FERRITES SINTERED ABOVE 1000-DEGREES-C
    BERMEJO, E
    LEMERCIER, T
    QUARTON, M
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (02) : 365 - 368
  • [34] SEEBECK COEFFICIENT OF YTTRIUM FROM 0-DEGREES-TO 1000-DEGREES-C
    JOHANSEN, HA
    MILLER, RC
    JOURNAL OF THE LESS-COMMON METALS, 1959, 1 (04): : 331 - 332
  • [35] DIFFUSION OF SILVER IN GALLIUM-ARSENIDE AT 1000-DEGREES-C
    TUCK, B
    ADEGBOYEGA, GA
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1980, 13 (03) : 433 - 440
  • [36] EXPANSION COEFFICIENTS UP TO 1000-DEGREES-C .3.
    SHERRATT, GG
    CHALLONER, AR
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1946, 154 (02): : P96 - P98
  • [37] HIGH-TEMPERATURE DEFORMATION OF DIOPSIDE .4. - PREDOMINANCE OF (110) GLIDE ABOVE 1000-DEGREES-C
    RATERRON, P
    DOUKHAN, N
    JAOUL, O
    DOUKHAN, JC
    PHYSICS OF THE EARTH AND PLANETARY INTERIORS, 1994, 82 (3-4) : 209 - 222
  • [38] *ELEKTRONENBEUGUNG AN METALL-EINKRISTALLEN BIS 1000-DEGREES-C
    MENZELKOPP, C
    MENZEL, E
    ZEITSCHRIFT FUR NATURFORSCHUNG SECTION A-A JOURNAL OF PHYSICAL SCIENCES, 1953, 8 (08): : 499 - 500
  • [39] OXIDATION OF COBALT-CHROMIUM ALLOYS AT 1000-DEGREES-C
    PRZYBYLSKI, K
    SZWAGIERCZAK, D
    ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 1979, 4 (1-2): : 61 - 76
  • [40] INVESTIGATIONS INTO SODIUM CORROSION OF AUSTENITIC MATERIALS AT 1000-DEGREES-C
    BORGSTEDT, HU
    FREES, G
    JESPER, H
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1989, 40 (09): : 525 - 531
12345