DIP-COATING CONDITIONS AND MODIFICATIONS OF LEAD TITANATE AND LEAD ZIRCONATE TITANATE FILMS

被引：90
|
作者：
TAKAHASHI, Y
YAMAGUCHI, K
机构：
[1] Department of Chemistry, Faculty of Engineering, Gifu University, Gifu, 501-11, Yanagido 1-1, Gifu City
来源：
JOURNAL OF MATERIALS SCIENCE | 1990年 / 25卷 / 09期
关键词：
D O I：
10.1007/BF00582465
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The modifications of dip-coated lead titanate (PT) and lead zirconate titanate (PZT) films strongly depend on the film thickness and the substrate in addition to the heat-treatment temperature. At 500 to 600 ° C, metastable paraelectric pyrochlore grew on glass plates (amorphous plates) when the thickness of the coated films produced by one coating cycle was below 100 nm, while ferroelectric perovskite formed on crystalline substrates or when thick films were coated on amorphous plates. This tendency is discussed in terms of an inhomogeneous reaction and the epitaxial effect. The perovskite PT films coated on single-crystal SrTiO3 plate at 700 ° C were strongly oriented to the c-axis. © 1990 Chapman and Hall Ltd.
引用
收藏
页码：3950 / 3955
页数：6
相关论文
共 50 条
  • [21] Influence of fatigue processes on the switching currents in lead titanate and lead zirconate-titanate films
    A. S. Sidorkin
    L. P. Nesterenko
    A. Yu. Pakhomov
    Physics of the Solid State, 2012, 54 : 1008 - 1010
  • [22] Effect of composition and preparation conditions on the microstructure of lead zirconate titanate films
    diCristoforo, A
    Mengucci, P
    Majni, G
    Severi, M
    Guerri, S
    Watts, BE
    Leccabue, F
    Seuret, D
    JOURNAL OF CRYSTAL GROWTH, 1996, 167 (3-4) : 644 - 648
  • [23] Influence of fatigue processes on the switching currents in lead titanate and lead zirconate-titanate films
    Sidorkin, A. S.
    Nesterenko, L. P.
    Pakhomov, A. Yu.
    PHYSICS OF THE SOLID STATE, 2012, 54 (05) : 1008 - 1010
  • [24] Hydrothermal synthesis of lead titanate and lead zirconate titanate electroceramic particles
    Suvaci, E
    Dogan, A
    Anderwson, J
    Adair, JH
    CHEMICAL ENGINEERING COMMUNICATIONS, 2003, 190 (5-8) : 843 - 852
  • [25] LEAD TITANATE ZIRCONATE EXPOSURE
    WEISS, RJ
    JOURNAL OF OCCUPATIONAL AND ENVIRONMENTAL MEDICINE, 1990, 32 (07) : 645 - 645
  • [26] Evolution of the switching current during the accumulation of fatigue in lead titanate and lead zirconate titanate thin films
    Sidorkin A.S.
    Nesterenko L.P.
    Pakhomov A.Y.
    Sidorkin A.A.
    Matveev N.N.
    Bulletin of the Russian Academy of Sciences: Physics, 2011, 75 (10) : 1304 - 1308
  • [27] Hydrothermal synthesis of lead zirconate titanate (PZT) and lead lanthanum zirconate titanate (PLZT) nanopowders
    Nualpralaksana, S
    Phanichphant, S
    Hengst, M
    Heimann, RB
    CFI-CERAMIC FORUM INTERNATIONAL, 2001, 78 (05): : E34 - E38
  • [28] FERROELECTRICITY IN SPUTTERED LEAD ZIRCONATE-TITANATE FILMS
    MACBETH, JW
    LUPFER, DA
    AMERICAN CERAMIC SOCIETY BULLETIN, 1968, 47 (04): : 389 - &
  • [29] Nanostructured heterophase thin films of lead zirconate titanate
    Afanasjev, V. P.
    Petrov, A. A.
    PHYSICS OF THE SOLID STATE, 2009, 51 (07) : 1332 - 1336
  • [30] Nanostructured heterophase thin films of lead zirconate titanate
    V. P. Afanasjev
    A. A. Petrov
    Physics of the Solid State, 2009, 51 : 1332 - 1336
12345