OBSERVATIONS CONCERNING STRESS-CORROSION CRACK-PROPAGATION IN A PURE ALZNMG3 ALLOY

被引：0

作者：

RICHTER, J ^{[1
]}

KAESCHE, H ^{[1
]}

机构：

[1] UNIV ERLANGEN NURNBERG,INST WERKSTOFFWISSENSCH,LEHRSTUHL KORROSION & OBERFLACHENTECH,D-8520 ERLANGEN,FED REP GER

来源：

WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION | 1977年 / 28卷 / 09期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

引用

页码：602 / 606

页数：5

共 50 条

[31] LOW-PH STRESS-CORROSION CRACK-PROPAGATION IN API X-65 LINE PIPE STEEL
HARLE, BA
BEAVERS, JA
CORROSION, 1993, 49 (10) : 861 - 863
[32] STRESS-CORROSION AND ACOUSTIC-EMISSION DURING TENSILE CRACK-PROPAGATION IN WHIN SILL DOLERITE AND OTHER BASIC ROCKS
MEREDITH, PG
ATKINSON, BK
GEOPHYSICAL JOURNAL OF THE ROYAL ASTRONOMICAL SOCIETY, 1983, 75 (01): : 1 - &
[33] INFLUENCE OF MICROSTRUCTURE AND ELECTRODE POTENTIAL UPON THE VELOCITY OF STRESS-CORROSION CRACKS OF A PURE ALZNMG3-ALLOY IN AN 1-M NACL-SOLUTION
RICHTER, J
KAESCHE, H
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1981, 32 (07): : 289 - 295
[34] STRESS-CORROSION FRACTURE OF ZIRCALOY CLADDING IN FUEL-RODS SUBJECTED TO POWER INCREASES - MODEL FOR CRACK-PROPAGATION AND THE FAILURE THRESHOLD STRESS
SMITH, E
MILLER, AK
JOURNAL OF NUCLEAR MATERIALS, 1979, 80 (02) : 291 - 302
[35] Multiscale investigation of stress-corrosion crack propagation mechanisms in oxide glasses
Pallares, Gael
George, Matthieu
Ponson, Laurent
Chapuliot, Stephane
Roux, Stephane
Ciccotti, Matteo
CORROSION REVIEWS, 2015, 33 (06) : 501 - 514
[36] CORROSION FATIGUE CRACK-PROPAGATION IN ALUMINUM-7-PERCENT MAGNESIUM ALLOY
FORD, FP
CORROSION, 1979, 35 (07) : 281 - 287
[37] A STUDY OF THE MECHANISM OF STRESS-CORROSION CRACK-PROPAGATION IN AISI 4340 STEEL IN AQUEOUS 3.5 WT-PERCENT NACL SOLUTION
KANG, IW
CHOI, JK
PYUN, SI
STEEL RESEARCH, 1987, 58 (12): : 565 - 569
[38] Investigations on the Intercrystalline Corrosion and Stress Corrosion Cracking of a Pure AlZnMg2-Alloy in NaCl-Solution.
Richter, J.
Hornig, W.
Kaesche, H.
Werkstoffe und Korrosion, 1984, 35 (01): : 23 - 27
[39] Poissonian random-process model for the initiation of stress-corrosion crack propagation
Akashi M.
Zairyo to Kankyo/ Corrosion Engineering, 2010, 59 (09): : 312 - 319
[40] RESISTANCE TO CRACK-PROPAGATION OF MARAGING STEEL-N18K9M5T UNDER STRESS-CORROSION CONDITIONS
SERGEEVA, TK
ANGELOVSKAYA, LM
MALKIN, VI
POKIDYSHEV, VV
METAL SCIENCE AND HEAT TREATMENT, 1976, 18 (9-10) : 792 - 795

← 1 2 3 4 5 →