NEW AMORPHOUS AL-NI-FE AND AL-NI-CO ALLOYS

被引:19
|
作者
INOUE, A
HORIO, Y
MASUMOTO, T
机构
[1] Institute for Materials Research, Tohoku University
[2] Technical Development Laboratory, YAMAHA Corp., Shizuoka 438-01, Toyooka-mura, Iwata-gun
来源
MATERIALS TRANSACTIONS JIM | 1993年 / 34卷 / 01期
关键词
ALUMINUM BASE ALLOY; AMORPHOUS PHASE; COEXISTENT AMORPHOUS AND FCC-AL PHASES; RAPID SOLIDIFICATION; ALUMINUM-TRANSITION METAL SYSTEM; HIGH MECHANICAL STRENGTH; GOOD DUCTILITY;
D O I
10.2320/matertrans1989.34.85
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
New amorphous alloys were found to form by melt spinning in Al-Ni-Fe and Al-Ni-Co systems without lanthanide (Ln), Zr and Nb, which are known to be glass-forming elements for Al-based alloys. Coexistent amorphous and Al phases, and the amorphous phase also formed in the ranges of 0 to 14 at% Ni and 0 to 10%Fe or 0 to 14%Co. The mixed phase alloys containing more than 87%Al as well as the amorphous single phase alloys have good bending ductility. Tensile fracture strength (sigma(f)) and Vickers hardness (H(v)) for the amorphous single phase are in the range 870 to 1070 MPa and 280 to 320, respectively. With decreasing cooling rate, the structure changes to Al and amorphous phases. Sigma(f) and H(v) increase to 1270 MPa and 360 without losing ductility in the mixed state where the volume fraction of the Al phase is about 20% and the particle size and interparticle spacing are about 10 nm and 30 nm, respectively. From the similarity in the mixed structure between the present alloys and the previously reported Al-Ni-Ln alloys, it is presumed that the increase in sigma(f) for the mixed phase alloys is due to the increase in strength of the Al particles resulting from the absence of internal defects as well as to the effective barrier of the Al particles against shear deformation of the amorphous matrix.
引用
收藏
页码:85 / 88
页数:4
相关论文
共 50 条
  • [31] The adsorption of Xe and Ar on quasicrystalline Al-Ni-Co
    Trasca, RA
    Ferralis, N
    Diehl, RD
    Cole, MW
    JOURNAL OF PHYSICS-CONDENSED MATTER, 2004, 16 (29) : S2911 - S2921
  • [32] Electronic valence bands in decagonal Al-Ni-Co
    Theis, W
    Rotenberg, E
    Franke, KJ
    Gille, P
    Horn, K
    PHYSICAL REVIEW B, 2003, 68 (10):
  • [33] ALCHEMI STUDIES ON Al-Ni-Co DECAGONAL QUASICRYSTALS
    Saitoh, K.
    Tanaka, M.
    Tsai, A. P.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2002, 58 : C236 - C236
  • [34] Nanocrystallization in Al-based amorphous Al-Ni-Fe-La alloys
    Bakhteeva N.D.
    Nanotechnologies in Russia, 2010, 5 (03): : 235 - 249
  • [35] Disordered quasicrystals: diffuse scattering in decagonal Al-Ni-Fe
    Weidner, E
    Frey, F
    Lei, JL
    Pedersen, B
    Paulmann, C
    Morgenroth, W
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2004, 37 : 802 - 807
  • [36] Atomic dynamics in decagonal Al-Ni-Co quasicrystals
    Gähler, F
    Hocker, S
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2004, 334 : 308 - 311
  • [37] Crystalline Textures on the Al-Ni-Co Quasicrystal Surface
    Erbudak, Mehmet
    Longchamp, Jean-Nicolas
    Weisskopf, Yves
    TURKISH JOURNAL OF PHYSICS, 2005, 29 (05): : 277 - 285
  • [38] Plastic deformation of decagonal Al-Ni-Co quasicrystals
    Feuerbacher, M
    Bartsch, M
    Grushko, B
    Messerschmidt, U
    Urban, K
    PHILOSOPHICAL MAGAZINE LETTERS, 1997, 76 (06) : 369 - 375
  • [39] Decagonal quasicrystals in Al-Ni-Co:: generality and particulars
    Grushko, B
    Döblinger, M
    ZEITSCHRIFT FUR KRISTALLOGRAPHIE, 2004, 219 (07): : 447 - 455
  • [40] The ordering of a Xe monolayer on quasicrystalline Al-Ni-Co
    Diehl, RD
    Ferralis, N
    Pussi, K
    Cole, MW
    Setyawan, W
    Curtarolo, S
    PHILOSOPHICAL MAGAZINE, 2006, 86 (6-8) : 863 - 868