ELECTROCHEMICAL HETEROGENEITY AND CORROSION-RESISTANCE OF A WELDED TITANIUM-ZIRCONIUM JOINT

The electrochemical behavior and corrosion resistance of various welded joints of zirconium alloy N-2.5 with commercial titanium VT1 made by the argon-arc method are studied. Electrochemical heterogeneity is studied by measuring the distribution of potentials over the surface, galvanic currents, and recording of polarization curves for different zones of a welded joint in 5% sulfuric acid solution at 340 K. It is established that electrochemical heterogeneity of the zones of an N-2.5 + VT1 welded joint leads to acceleration of the cathodic process in a welded joint and the anodic process along the fusion line from the titanium direction where the greatest hydrogenation of the metal and corrosion damage is correspondingly observed.