Chrome-free conversion layers on zinc alloy coatings - preliminary tests

被引：0
|
作者：
Winiarski, Juliusz [1 ]
Szczygiel, Bogdan [1 ]
机构：
[1] Wroclaw Univ Technol, Zaklad Inzynierii Powierzchni Katalizy & Korozji, Wroclaw, Poland
来源：
OCHRONA PRZED KOROZJA | 2009年 / 52卷 / 4-5期
关键词：
chromating; conversion coating; corrosion resistance; molybdate; citrate;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Molybdate conversion layers have been obtained on the Zn-Ni alloy electrogal-vanised steel from a solution containing sodium molybdate(VI) and sodium citrate, acidified with phosphoric acid. The layers were deposited at different bath temperatures and different pH values. Chromated samples were used as the reference in order to compare the corrosion resistance properties. The increasing bath's temperature causes decreasing corrosion resistance (bigger corrosion curents, smaller polarisation resistance) in 0,5 M NaCl environment. The best molybdate layers were obtained in temperature 25-40 degrees C. These layers are homogeneous and free of cracks.
引用
收藏
页码：174 / 176
页数：3
相关论文
共 50 条
  • [41] Electrochemical study on the corrosion resistance of CrIII-based conversion layers on zinc coatings
    Bellezze, T
    Roventi, G
    Fratesi, R
    SURFACE & COATINGS TECHNOLOGY, 2002, 155 (2-3): : 221 - 230
  • [42] Dry sliding wear behavior of hard-chrome and zinc-phosphate conversion coatings on steel substrates
    Kumar, Arun
    Rachwani, Harsh
    Singh, Manjesh Kumar
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY, 2024, 238 (06) : 662 - 675
  • [43] Effect of microstructure on the zinc phosphate conversion coatings on magnesium alloy AZ91
    Nguyen Van Phuong
    Moon, Sungmo
    Chang, Doyon
    Lee, Kyu Hwan
    APPLIED SURFACE SCIENCE, 2013, 264 : 70 - 78
  • [44] Effect of refining grain size on the corrosion behavior of Cr(III) conversion layers on zinc coatings
    Meng, Guozhe
    Zhang, Lei
    Shao, Yawei
    Zhang, Tao
    Wang, Fuhui
    Dong, Chaofang
    Li, Xiaogang
    SCRIPTA MATERIALIA, 2009, 61 (11) : 1004 - 1007
  • [45] Comparison of single and multilayer coatings based on ormosil and conversion layers for aluminum alloy corrosion inhibition
    Kachurina, O
    Metroke, TL
    Stesikova, E
    Knobbe, ET
    JOURNAL OF COATINGS TECHNOLOGY, 2002, 74 (926): : 43 - 48
  • [46] Studies on chrome free galvanic conversion coating on magnesium alloy AZ31B for space applications
    Parida, Benudhar
    Rani, R. Uma
    Sharma, A. K.
    SURFACE ENGINEERING, 2010, 26 (05) : 361 - 366
  • [47] Inhibited chromate-free conversion coatings for AMg5 aluminum alloy
    Chugunov, D. O.
    Kuzenkov, Yu. A.
    Rybakov, S. Yu.
    INTERNATIONAL JOURNAL OF CORROSION AND SCALE INHIBITION, 2023, 12 (04): : 2092 - 2100
  • [48] Formation of black chromate conversion coatings on pure and zinc alloy electrolytic deposits: Role of the main constituents
    Gigandet, MP
    Faucheu, J
    Tachez, M
    SURFACE & COATINGS TECHNOLOGY, 1997, 89 (03): : 285 - 291
  • [49] Modification of chromate-free conversion coatings on 1105 aluminum alloy to increase their protective properties
    Chugunov, D. O.
    Kuzenkov, Yu. A.
    Rybakov, S. Yu.
    INTERNATIONAL JOURNAL OF CORROSION AND SCALE INHIBITION, 2024, 13 (04): : 2255 - 2265
  • [50] Submicron free-chromate chemical conversion coatings on AMg-3 aluminum alloy
    Yu. A. Kuzenkov
    S. V. Oleinik
    A. S. Zimina
    L. P. Kazanskii
    V. N. Ivonin
    V. A. Karpov
    Protection of Metals and Physical Chemistry of Surfaces, 2016, 52 : 1175 - 1180
12345