HOST EFFECT FOR INTERCALATION OF CUCL2 IN MOLTEN-SALT

被引：9

作者：

INAGAKI, M ^{[1
]}

WANG, ZD ^{[1
]}

机构：

[1] TOYOHASHI UNIV TECHNOL,TOYOHASHI 441,JAPAN

来源：

CARBON | 1992年 / 30卷 / 06期

关键词：

INTERCALATION COMPOUNDS; HOST GRAPHITE; CUCL2;

D O I：

10.1016/0008-6223(92)90009-L

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A remarkable host effect on the intercalation of CuCl2 in a molten salt system of CUCl2-KCl was observed. Even after 12 days in the molten salt at 380-degrees-C, no graphite intercalation compounds (GICs) were obtained from the graphite films prepared from a polyimide Kapton, while from highly oriented pyrolytic graphite and kish graphite with similar physical sizes, GICs were obtained within one day and from natural graphite flakes with the size of 400-mu-m, within two hours. The graphite film containing more defects (H-film) was transformed to the stage-2 GIC at 500-degrees by applying Cl2 pressure, but the more perfect film (O-film) did not under the same condition.

引用

页码：869 / 872

页数：4

共 50 条

[21] Fuel Salt for the Molten-Salt Reactor
L. I. Ponomarev
M. B. Seregin
A. P. Parshin
S. A. Mel’nikov
A. A. Mikhalichenko
L. P. Zagorets
R. N. Manuilov
A. A. Rzheutskii
Atomic Energy, 2013, 115 : 5 - 10
[22] MOSSBAUER STUDY OF IRON CHLORIDE-GRAPHITE INTERCALATION COMPOUNDS SYNTHESIZED IN MOLTEN-SALT
WANG, ZD
INAGAKI, M
TAKANO, M
CARBON, 1991, 29 (03) : 423 - 427
[23] Molten-salt processing of BFPT
He, Jingyan
Comyn, Tim P.
Bell, Andrew J.
2007 SIXTEENTH IEEE INTERNATIONAL SYMPOSIUM ON THE APPLICATIONS OF FERROELECTRICS, VOLS 1 AND 2, 2007, : 410 - 412
[24] THE MOLTEN-SALT REACTOR ADVENTURE
MACPHERSON, HG
NUCLEAR SCIENCE AND ENGINEERING, 1985, 90 (04) : 374 - 380
[25] MOLTEN-SALT ELECTROWINNING OF LEAD
DUCATI, U
CAVALLOTTI, P
LEONARDIS, B
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1982, 129 (03) : C107 - C107
[26] RECHARGEABLE MOLTEN-SALT CELLS
CAIRNS, EJ
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1980, 127 (08) : C408 - C408
[27] MODEL FOR SURFACE OF A MOLTEN-SALT
GOODISMAN, J
PASTOR, RW
JOURNAL OF PHYSICAL CHEMISTRY, 1978, 82 (19): : 2078 - 2081
[28] ELECTROCHEMISTRY OF MOLTEN-SALT CORROSION
NISHIKATA, A
NUMATA, H
TSURU, T
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 146 (1-2): : 15 - 31
[29] MOLTEN-SALT CONFERENCE IN LYSEKIL
HOLMBERG, B
KEMISK TIDSKRIFT, 1978, 90 (10): : 48 - 49
[30] APPLICATIONS OF MOLTEN-SALT TECHNOLOGY
ITO, Y
DENKI KAGAKU, 1993, 61 (01): : 23 - 24

← 1 2 3 4 5 →