HOST EFFECT FOR INTERCALATION OF CUCL2 IN MOLTEN-SALT

被引：9

作者：

INAGAKI, M ^{[1
]}

WANG, ZD ^{[1
]}

机构：

[1] TOYOHASHI UNIV TECHNOL,TOYOHASHI 441,JAPAN

来源：

CARBON | 1992年 / 30卷 / 06期

关键词：

INTERCALATION COMPOUNDS; HOST GRAPHITE; CUCL2;

D O I：

10.1016/0008-6223(92)90009-L

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A remarkable host effect on the intercalation of CuCl2 in a molten salt system of CUCl2-KCl was observed. Even after 12 days in the molten salt at 380-degrees-C, no graphite intercalation compounds (GICs) were obtained from the graphite films prepared from a polyimide Kapton, while from highly oriented pyrolytic graphite and kish graphite with similar physical sizes, GICs were obtained within one day and from natural graphite flakes with the size of 400-mu-m, within two hours. The graphite film containing more defects (H-film) was transformed to the stage-2 GIC at 500-degrees by applying Cl2 pressure, but the more perfect film (O-film) did not under the same condition.

引用

页码：869 / 872

页数：4

共 50 条

[1] INTERCALATION REACTIONS IN MOLTEN-SALT SYSTEMS
INAGAKI, M
SYNTHETIC METALS, 1990, 34 (1-3) : 15 - 20
[2] Intercalation of CuCl2 into expanded graphite
Chuan, X
Chen, D
Zhou, X
CARBON, 1997, 35 (02) : 311 - 313
[3] ELECTROCHEMICAL STUDIES OF INTERCALATION COMPOUNDS FOR MOLTEN-SALT BATTERIES
VASSORT, G
GAUTHIER, M
BELANGER, A
ADAMS, WA
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1980, 127 (08) : C352 - C352
[4] THERMODYNAMIC INVESTIGATIONS ON MOLTEN-SALT SOLUTIONS - THE CUCL-ZNCL2 AND CUCL-CDCL2 SYSTEMS
SLABY, H
POLISH JOURNAL OF CHEMISTRY, 1980, 54 (09) : 1641 - 1646
[5] BiCl3, CuCl2 intercalation into HOPG
Kanazawa Institute of Technology, 7-1 Ohgigaoka Nonoichi-machi, Isikawa 921-8501, Japan
Funtai Oyobi Fummatsu Yakin, 2006, 12 (955-959):
[6] THERMODYNAMIC INVESTIGATION ON MOLTEN-SALT SOLUTIONS - THE CUCL-INCL SYSTEM
SLABY, H
POLISH JOURNAL OF CHEMISTRY, 1980, 54 (10) : 1865 - 1868
[7] THERMODYNAMIC INVESTIGATION OF MOLTEN-SALT SOLUTIONS - SYSTEM CUCL-TLCL
SLABY, H
ROCZNIKI CHEMII, 1974, 48 (06): : 915 - 920
[8] Synthesis of CuCl2-Graphite Intercalation Compounds in Molten Salt and Their Formation Mechanism
Sheng Y.
Zheng P.
Zhang Z.
Li W.
Huanan Ligong Daxue Xuebao/Journal of South China University of Technology (Natural Science), 2019, 47 (12): : 99 - 105
[9] The electrical property and its mechanism of intercalation compounds of CuCl2
Chuan, Xiu-Yun
Chen, Dai-Zhang
Zhou, Xun-Ruo
Jiang, Jia-Ji
Li, He-Jun
Wuli Xuebao/Acta Physica Sinica, 1999, 48 (06): : 1136 - 1137
[10] Preparation and Structural Investigation of CuCl2 Graphite Intercalation Compounds
BIN Xiaopei~(1
ActaGeologicaSinica(EnglishEdition), 2008, (05) : 1056 - 1060

← 1 2 3 4 5 →