MECHANISMS OF FATIGUE FRACTURE IN SHORT GLASS FIBER-REINFORCED POLYMERS

被引：50
|
作者：
LANG, RW [1 ]
MANSON, JA [1 ]
HERTZBERG, RW [1 ]
机构：
[1] LEHIGH UNIV,MAT RES CTR,BETHLEHEM,PA 18015
来源：
JOURNAL OF MATERIALS SCIENCE | 1987年 / 22卷 / 11期
关键词：
D O I：
10.1007/BF01133353
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
42
引用
收藏
页码：4015 / 4030
页数：16
相关论文
共 50 条
  • [41] ORIENTATION EFFECTS AND RHEOLOGY OF SHORT GLASS FIBER-REINFORCED THERMOPLASTICS
    LAUN, HM
    COLLOID AND POLYMER SCIENCE, 1984, 262 (04) : 257 - 269
  • [42] Service life behavior of short glass fiber-reinforced thermoplastics
    Michaeli, Walter
    Hopmann, Christian
    Michaeli
    Dering, Jan Peter
    Kremer, Hendrik
    Konstruktion, 2011, (05):
  • [43] Effect of chemical ageing on fatigue life of short glass fiber-reinforced Polyamide 6,6
    Lottier, S.
    Tence-Girault, S.
    Gervat, L.
    Saintier, N.
    Miquelard-Garnier, G.
    Fayolle, B.
    POLYMER DEGRADATION AND STABILITY, 2023, 208
  • [44] Fracture behavior of short fiber-reinforced CAD/CAM inlay restorations after cyclic fatigue aging
    S. Garoushi
    D. Barlas
    P. K. Vallittu
    M. B. Uctasli
    L. Lassila
    Odontology, 2024, 112 : 138 - 147
  • [45] Multi-scale analysis of short glass fiber-reinforced polypropylene under monotonic and fatigue loading
    Imaddahen, Mohamed A.
    Shirinbayan, Mohammadali
    Ayari, Houssem
    Foucard, Mathieu
    Tcharkhtchi, Abbas
    Fitoussi, Joseph
    POLYMER COMPOSITES, 2020, 41 (11) : 4649 - 4662
  • [46] Fracture behavior of short fiber-reinforced CAD/CAM inlay restorations after cyclic fatigue aging
    Garoushi, S.
    Barlas, D.
    Vallittu, P. K.
    Uctasli, M. B.
    Lassila, L.
    ODONTOLOGY, 2024, 112 (01) : 138 - 147
  • [47] Mechanism of fatigue fracture of glass fiber reinforced nylon 66
    Odaka, S
    Kuriyama, T
    Kotaki, M
    Narisawa, I
    DESIGN AND MANUFACTURING OF COMPOSITES, 1998, : 99 - 102
  • [48] Study on fatigue fracture mechanisms of short fiber reinforced PET composite by acoustic emission method
    Suzuki, Megumu, 1600, (55):
  • [49] FRACTURE MECHANISMS OF THE FIBER MATRIX INTERFACIAL BOND IN FIBER-REINFORCED POLYMER COMPOSITES
    LATOUR, RA
    BLACK, J
    MILLER, B
    SURFACE AND INTERFACE ANALYSIS, 1991, 17 (07) : 477 - 484
  • [50] FRACTURE OF FIBER-REINFORCED MATERIALS
    GAO, YC
    MAI, YW
    COTTERELL, B
    ZEITSCHRIFT FUR ANGEWANDTE MATHEMATIK UND PHYSIK, 1988, 39 (04): : 550 - 572
12345