STRUCTURE FORMATION AND MECHANICAL-BEHAVIOR OF AL2O3/ZRO2(Y2O3) DISPERSION CERAMICS

被引：1
|
作者：
BISCHOFF, S
MICHALOWSKY, L
WERNER, G
PIPPEL, E
WOLTERSDORF, J
机构：
[1] Bergakademie Freiberg, Sektion Werkstoffwissenschaft, DDR-9200 Freiberg
[2] Institut für Festkörperphysik und Elektronenmikroskopie der Akademie der Wissenschaften der DDR, DDR-4050 Halle, Weinberg
来源：
CERAMICS INTERNATIONAL | 1990年 / 16卷 / 02期
关键词：
D O I：
10.1016/0272-8842(90)90082-Q
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The microstructure and the mechanical properties of alumina ceramics doped with yttria-stabilized tetragonal zirconia were investigated depending on the quality of the raw material and the process parameters of specimen production. Doping with 30 wt% ZrO2 (Y2O3) resulted in a strength of about 530 MPa, which was increased by about 10% by means of nitrogen cooling. The size of the ZrO2 particles varied between 0·4 and 0·5 μm. Electron microscopy studies revealed a partial transformation of the ZrO2 particles and the rather inhomogeneous transformation behaviour depending on the grain size. © 1990.
引用
收藏
页码：121 / 127
页数：7
相关论文
共 50 条
  • [41] Phase Transformations of Electrochemically Prepared Precursors of the TiO2–ZrO2–Y2O3 and TiO2–Al2O3–ZrO2–Y2O3 Oxide Systems
    A. F. Dresvyannikov
    E. V. Petrova
    L. I. Kashfrazyeva
    A. I. Khairullina
    Inorganic Materials, 2023, 59 : 742 - 748
  • [42] Metastable phase formation during flame spray pyrolysis of ZrO2(Y2O3)-Al2O3 nanoparticles
    Suffner, J.
    Wang, D.
    Kuebel, C.
    Hahn, H.
    SCRIPTA MATERIALIA, 2011, 64 (08) : 781 - 784
  • [43] Development of microstructure in Si3N4 ceramics formed with additions of ZrO2, Y2O3 and Al2O3
    Falk, L.K.L.
    Key Engineering Materials, 1994, 89-91 : 489 - 494
  • [44] DEVELOPMENT OF MICROSTRUCTURE IN SI3N4 CERAMICS FORMED WITH ADDITIONS OF ZRO2, Y2O3 AND AL2O3
    FALK, LKL
    SILICON NITRIDE 93, 1994, 89-9 : 489 - 493
  • [45] Medical Ceramics from Powders of the System Al2O3–ZrO2–Y2O3 Obtained on an Installation of Nanospray Drying
    Lyamina G.V.
    Ilela A.E.
    Dvilis E.S.
    Petyukevich M.A.
    Tolkachev O.S.
    Nanotechnologies in Russia, 2018, 13 (5-6): : 337 - 343
  • [46] Preparation and mechanical properties of ZrO2/Al2O3 porous ceramics
    Jiang Hao-ran
    Lin Shuo
    Zhang Kang-fei
    Wang Hai-yan
    Wang Jia-qi
    He Xiu-lan
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2021, 49 (05): : 157 - 162
  • [47] The α-Al2O3 fibers in ZrO2-Y2O3-Al2O3 ceramics
    Savchenko, N.L.
    Sablina, T.Yu.
    Mel'nikov, A.G.
    Korolev, P.V.
    Kul'kov, S.N.
    Ogneupory i Tekhnicheskaya Keramika, 2005, (10): : 13 - 15
  • [48] Comparing the thermodynamic behaviour of Al(l)+ZrO2(4% Y2O3) and Al(l)+Al2O3
    Copland, Evan
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2006, 97 (08) : 1108 - 1114
  • [49] Interaction of SiC with Al2O3−(t + m)ZrO2(Y2O3) Oxide Composition
    M. G. Frolova
    A. S. Lysenkov
    S. N. Perevislov
    N. V. Petrakova
    K. A. Kim
    M. A. Sevost’yanov
    A. Yu. Ivannikov
    M. D. Mel’nikov
    Yu. F. Kargin
    Russian Journal of Inorganic Chemistry, 2023, 68 (8) : 1077 - 1083
  • [50] 新型Y2O3/ZrO2—Al2O3复合材料的制备
    董群满
    稀土信息, 1993, (08) : 12 - 12
12345