ACTIVITY AND THERMORESISTANCE OF FUSED IRON CATALYSTS FOR AMMONIA-SYNTHESIS

被引：14
|
作者：
KOWALCZYK, Z
JODZIS, S
机构：
[1] Department of Chemistry, Warsaw University of Technology, PL-00-664 Warsaw
来源：
APPLIED CATALYSIS | 1990年 / 58卷 / 01期
关键词：
D O I：
10.1016/S0166-9834(00)82276-9
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The activity and thermoresistance of five industrial catalysts were examined. Kinetic measurements were carried out in an isothermal, flow differential reactor under 10.0 MPa in the 400-520°C temperature range. In thermoresistance tests, overheating of the catalysts was carried out at 650°C for 24 h, or at 620°C for 24 to 192 h. The relationships obtained during both experimental tests were similar, with 24-h operating at 650°C giving a similar activity decrease as ageing for 192 h at 620°C. The chemical composition of the catalysts (XRF) was determined. © 1990.
引用
收藏
页码：29 / 34
页数：6
相关论文
共 50 条
  • [21] CHARACTERIZATION AND AMMONIA-SYNTHESIS ACTIVITY OF RUTHENIUM ZEOLITE CATALYSTS
    CISNEROS, MD
    LUNSFORD, JH
    JOURNAL OF CATALYSIS, 1993, 141 (01) : 191 - 205
  • [22] DETERMINATION OF PASSIVATION LAYER THICKNESS IN IRON CATALYSTS FOR AMMONIA-SYNTHESIS
    BARANSKI, A
    PATTEK, A
    REIZER, A
    BULLETIN DE L ACADEMIE POLONAISE DES SCIENCES-SERIE DES SCIENCES CHIMIQUES, 1978, 26 (05): : 353 - 358
  • [23] IRON COBALT CATALYSTS WITH ADDITIONS OF CERIUM OXIDE FOR AMMONIA-SYNTHESIS
    AGEEVA, IV
    KRYLOVA, AV
    JOURNAL OF APPLIED CHEMISTRY OF THE USSR, 1992, 65 (09): : 1758 - 1760
  • [24] EFFECT OF PRESSURE ON THE REDUCTION RATE OF A FUSED IRON CATALYST FOR AMMONIA-SYNTHESIS
    BARANSKI, A
    HAJDUK, J
    HESS, D
    BAERNS, M
    APPLIED CATALYSIS, 1989, 54 (02): : 111 - 117
  • [25] KINETICS OF WET ATMOSPHERE REDUCTION OF A FUSED IRON CATALYST FOR AMMONIA-SYNTHESIS
    BARANSKI, A
    KOTARBA, A
    LAGAN, JM
    APPLIED CATALYSIS, 1991, 71 (02): : L1 - L4
  • [26] Effect of iron oxide precursor on the properties and ammonia synthesis activity of fused iron catalysts
    Jafari, Ali
    Ebadi, Abbas
    Sahebdelfar, Saeed
    REACTION KINETICS MECHANISMS AND CATALYSIS, 2019, 126 (01) : 307 - 325
  • [27] Effect of iron oxide precursor on the properties and ammonia synthesis activity of fused iron catalysts
    Ali Jafari
    Abbas Ebadi
    Saeed Sahebdelfar
    Reaction Kinetics, Mechanisms and Catalysis, 2019, 126 : 307 - 325
  • [28] CARRIER EFFECT ON THE IRON ACTIVITY IN THE REACTION OF THE AMMONIA-SYNTHESIS
    YATSIMIRSKY, VK
    KHO, ZZ
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA B-GEOLOGICHNI KHIMICHNI TA BIOLOGICHNI NAUKI, 1988, (12): : 42 - 43
  • [29] MELTED IRON CATALYSTS OF AMMONIA-SYNTHESIS WITH DIFFERENT CONTENT OF BIVALENT AND TRIVALENT IRON
    DVORNIK, OS
    STRELTSOV, OA
    ARTYUKH, YN
    UKRAINSKII KHIMICHESKII ZHURNAL, 1977, 43 (04): : 375 - 380
  • [30] ACTIVITY AND THERMAL-STABILITY OF PRECIPITATED IRON CATALYSTS FOR AMMONIA-SYNTHESIS, PROMOTED WITH URANIUM OXIDES
    BADIK, VS
    LYUBCHENKO, YA
    SERGEEVA, AN
    DMITRENKO, LM
    JOURNAL OF APPLIED CHEMISTRY OF THE USSR, 1974, 47 (10): : 2239 - 2241
12345