Analysis of Cracking in Glass Molds Made of Cast Iron

被引：0
|
作者：
Leushin, I. O. [1 ]
Chistyakov, D. G. [1 ]
机构：
[1] Nizhnii Novgorod State Univ, Pr Gagarina 23, Nizhnii Novgorod 630600, Russia
来源：
RUSSIAN METALLURGY | 2014年 / 09期
关键词：
D O I：
10.1134/S0036029514090110
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The cracking in the parts of cast iron molds intended for glass is considered, and this cracking substantially affects the operation of glass-blowing equipment, maintainability, and the replacement of mold sets. The processes that cause cracking in the parts of glass molds and initiate crack growth are studied.
引用
收藏
页码：768 / 771
页数：4
相关论文
共 50 条
  • [31] Failure analysis of a truck diesel engine crankshaft made from spheroidal cast iron
    Xu X.-L.
    Yu Z.-W.
    Journal of Failure Analysis and Prevention, 2011, 11 (04) : 332 - 336
  • [32] Fatigue analysis-based numerical design of stamping tools made of cast iron
    Ben Slima, K.
    Penazzi, L.
    Mabru, C.
    Ronde-Oustau, F.
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2013, 67 (5-8): : 1643 - 1650
  • [33] Fatigue analysis-based numerical design of stamping tools made of cast iron
    K. Ben Slima
    L. Penazzi
    C. Mabru
    F. Ronde-Oustau
    The International Journal of Advanced Manufacturing Technology, 2013, 67 : 1643 - 1650
  • [34] RAPID METHOD OF DETERMINING COMPOSITION OF CAST-IRON MOLDS (EXCHANGE OF EXPERIENCE)
    BARBAKAD.DF
    MEPARIDZ.NA
    INDUSTRIAL LABORATORY, 1967, 33 (09): : 1294 - &
  • [35] Technology for Making Partially Fusible Permanent Molds to Cast Iron Grinding Balls
    K. N. Vdovin
    I. V. Ponurko
    M. V. Shubina
    Metallurgist, 2001, 45 : 167 - 170
  • [36] INCREASING SERVICE LIFE OF INGOT MOLDS OF CAST-IRON ALLOYED WITH ALUMINUM
    SHASHKOV, VB
    NEPOMNYASHCHII, AG
    SHCHERBILIS, IA
    SHASHKOVA, VK
    BURLAK, MS
    METAL SCIENCE AND HEAT TREATMENT, 1975, 17 (5-6) : 421 - 424
  • [37] Spheroid graphite cast iron specimens with defects cracking investigation
    Leonavicius, M.
    Bobyliov, K.
    Krenevicius, A.
    Stupak, S.
    MECHANIKA, 2008, 69 (01): : 13 - 18
  • [38] Caustic stress corrosion cracking of a graphite cast iron component
    Raman, RKS
    Muddle, BC
    ENGINEERING FAILURE ANALYSIS, 2004, 11 (02) : 199 - 206
  • [39] Cracking due to combined TMF and HCF loading in cast iron
    Hosseini, E.
    Holdsworth, S. R.
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 99 : 279 - 285
  • [40] A METALLOGRAPHIC STUDY OF GRAY CAST-IRON SOLIDIFIED IN OSCILLATING AND ROTATING MOLDS
    TORRESSANCHEZ, R
    GRUZLESKI, JE
    METALLOGRAPHY, 1980, 13 (02): : 143 - 155
12345