INFLUENCE OF STRESS, TEMPERATURE, AND FRACTURE TOUGHNESS ON CRACK-PROPAGATION BEHAVIOR OF A HIGH-STRENGTH STEEL AT PULSATING TENSION

被引：3

作者：

SCHMIDTMANN, E ^{[1
]}

HENDERS, S ^{[1
]}

机构：

[1] RHEIN WESTFAL TH AACHEN,INST EISENHUTTENKUNDE,D-5100 AACHEN,FED REP GER

来源：

ARCHIV FUR DAS EISENHUTTENWESEN | 1977年 / 48卷 / 11期

关键词：

D O I：

10.1002/srin.197705071

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

页码：585 / 589

页数：5

共 50 条

[1] INFLUENCE OF THE ENVIRONMENT ON THE CRACKING TOUGHNESS AND CRACK-PROPAGATION IN HIGH-STRENGTH STEELS
KUSTER, F
BOHNENKAMP, K
ENGELL, HJ
[J]. WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1978, 29 (12): : 792 - 799
[2] RAPID CRACK-PROPAGATION IN A HIGH-STRENGTH STEEL
HAHN, GT
HOAGLAND, RG
ROSENFIELD, AR
SEJNOHA, R
[J]. METALLURGICAL TRANSACTIONS, 1974, 5 (02): : 475 - 482
[3] TENSION TENSION FATIGUE CRACK-PROPAGATION IN HIGH-STRENGTH, LOW-ALLOY STEEL SHEETS
MAZHAR, AA
KHOKHAR, EA
KHAN, AQ
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 1988, 4 (01) : 16 - 21
[4] ENVIRONMENTAL INFLUENCE ON THE NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION BEHAVIOR OF A HIGH-STRENGTH STEEL
HENAFF, G
PETIT, J
BOUCHET, B
[J]. INTERNATIONAL JOURNAL OF FATIGUE, 1992, 14 (04) : 211 - 218
[5] ROLE OF FRACTURE TOUGHNESS IN LOW-CYCLE FATIGUE CRACK-PROPAGATION FOR HIGH-STRENGTH ALLOYS
CROOKER, TW
[J]. REPORT OF NRL PROGRESS, 1972, (MAY): : 23 - &
[6] FATIGUE CRACK-PROPAGATION CHARACTERISTIC AND FATIGUE FRACTURE-TOUGHNESS IN 780 MPA GRADE HIGH-STRENGTH STEEL WELDMENTS AT LOW-TEMPERATURE
SATO, K
YOKOBORI, T
IGARASHI, H
NISHIDA, S
MASUMOTO, H
[J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1983, 47 (07) : 596 - 602
[7] DEPENDENCE OF THE FRACTURE TOUGHNESS OF HIGH-STRENGTH STEEL ON CRACK VELOCITY
BILEK, Z
[J]. SCRIPTA METALLURGICA, 1978, 12 (12): : 1101 - 1106
[8] INFLUENCE OF STRESS RATIO ON THRESHOLD LEVEL FOR FATIGUE CRACK-PROPAGATION IN HIGH-STRENGTH STEELS
OHTA, A
SASAKI, E
[J]. ENGINEERING FRACTURE MECHANICS, 1977, 9 (02) : 307 - 315
[9] EFFECT OF DENSITY ON TENSILE-STRENGTH, FRACTURE-TOUGHNESS, AND FATIGUE CRACK-PROPAGATION BEHAVIOR OF SINTERED STEEL
FLECK, NA
SMITH, RA
[J]. POWDER METALLURGY, 1981, 24 (03) : 121 - 125
[10] INFLUENCE OF DYNAMIC FRACTURE-TOUGHNESS ON DYNAMIC CRACK-PROPAGATION
HODULAK, L
KOBAYASHI, AS
EMERY, AF
[J]. ENGINEERING FRACTURE MECHANICS, 1980, 13 (01) : 85 - 93

← 1 2 3 4 5 →