Prediction of Ferrite Content in Austenitic Cr-Ni Steel Castings During Production

被引：1
|
作者：
Senberger, J. [1 ]
Pernica, V. [1 ]
Kana, V. [1 ]
Zadera, A. [1 ]
机构：
[1] Brno Univ Technol, Fac Mech Engn, Inst Mfg Technol, Foundry Dept,Tech 2, Brno, Czech Republic
来源：
ARCHIVES OF FOUNDRY ENGINEERING | 2018年 / 18卷 / 03期
关键词：
Solidification; Metallography; Austenitic steel; Austenite; Ferrite; DeLong diagram;
D O I：
10.24425/123608
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Determination of the ferrite content in austenitic steels, which solidified under defined conditions. Ferrite content in austenitic matrix was determined from samples with wall thickness of 60 mm. Measured ferrite contents served to propose the regression equations for the calculation of the ferrite content in steels with Cr content of 18 up to 22 % and Ni of 9 up to 11 %. An additional regression equation was proposed for steels with a higher Ni content. The proposed regression equations have been checked up on the operating melts. In conclusion, the ferrite content in the axis of the casting of wall thickness of 500 mm has been calculated and it was compared to the ferrite determined in the usual way from the cast-on test.
引用
收藏
页码：91 / 94
页数：4
相关论文
共 50 条
  • [1] SURFACE TREATMENT OF AUSTENITIC CR-NI STEEL
    YAMAGUCHI, S
    [J]. ZEITSCHRIFT FUR METALLKUNDE, 1976, 67 (02): : 135 - 136
  • [2] CHEMICAL DECONTAMINATION STUDIES OF AUSTENITIC CR-NI STEEL
    MATSCHEI, B
    TAGNATZ, G
    VOLTER, J
    [J]. KERNENERGIE, 1991, 34 (04): : 150 - 152
  • [3] PRODUCTION TECHNIQUE AND PROPERTIES OF AUSTENITIC Cr-Ni STAINLESS STEEL POWDERS.
    Dautzenberg, H.
    Gesell, H.
    [J]. Powder Metallurgy, 1976, 8 (01): : 14 - 17
  • [4] EBSD Analysis of an Austenitic Cr-Ni Steel Laser Weld
    Pugacheva, N. B.
    Zadvorkin, S. M.
    Michurov, N. S.
    [J]. PHYSICS OF METALS AND METALLOGRAPHY, 2022, 123 (08): : 791 - 796
  • [5] GRAIN COARSENING IN HOT DEFORMED AUSTENITIC CR-NI STEEL
    KASPAR, R
    VANZIJL, H
    DISTL, JS
    PAWELSKI, O
    [J]. ARCHIV FUR DAS EISENHUTTENWESEN, 1984, 55 (05): : 229 - 234
  • [6] Laser Surface Melting of Austenitic Cr-Ni Stainless Steel
    Stavrev, Dimitar
    Dikova, Tsanka
    Shtarbakov, Vladimir
    Milkov, Mario
    [J]. ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES II, PTS 1 AND 2, 2011, 264-265 : 1287 - +
  • [7] CARBIDE EQUILIBRIA IN AUSTENITIC CR-NI STEEL AT 1273-K
    NIEMCZURA, Z
    KUNZE, J
    [J]. STEEL RESEARCH, 1990, 61 (02): : 77 - 83
  • [8] EFFECT OF GRAIN SIZE ON CREEP RATE OF A CR-NI AUSTENITIC STEEL
    MYERS, J
    WILLOUGH.G
    [J]. METALLURGIA, 1966, 73 (435): : 3 - &
  • [9] MICROANALYTIC DETERMINATION OF THE AMOUNT OF PRIMARY FERRITE AND OF THE DISTRIBUTION COEFFICIENTS OF AUSTENITIC CR-NI AND CR-NI-MO STEELS
    SIEGEL, U
    HAAS, A
    [J]. NEUE HUTTE, 1984, 29 (06): : 211 - 216
  • [10] Strengthening of Stable Cr-Ni Austenitic Stainless Steel under Thermomechanical Treatments
    Akkuzin, S. A.
    Litovchenko, I. Yu.
    Tyumentsev, A. N.
    [J]. PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES 2017 (AMHS'17), 2017, 1909
12345