DIELECTRIC-PROPERTIES OF POLY[BIS(TRIFLUOROETHOXY)PHOSPHAZENE] AND POLY[BIS(M-METHYLPHENOXY)PHOSPHAZENE]

被引：4
|
作者：
MORIYA, K
NISHIBE, Y
YANO, S
机构：
[1] Department of Chemistry, Faculty of Engineering, Gifu University, Gifu, 501-11, Yanagido
来源：
MACROMOLECULAR CHEMISTRY AND PHYSICS | 1994年 / 195卷 / 02期
关键词：
D O I：
10.1002/macp.1994.021950228
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
Dielectric properties of Poly[bis(trifluoroethoxy)phosphazene] (PFEP) and poly[bis(m-methylphenoxy)phosphazene] (PmMPP) were studied in a temperature range from -195 to 120-degrees-C and at several frequencies between 0,1 and 100 kHz. In PFEP, two relaxations, an a relaxation above the glass transition temperature (T(g)) and a beta relaxation below T(g), which are related to a glass-rubber transition and a local molecular motion of short segments, respectively, were observed. However, PmMPP shows no beta relaxation. From the above dielectric results, it was concluded that side groups play an important role in molecular motion of the polyphosphazenes. In PmMPP a gamma' relaxation was found below T(g) by immersing the polymers into water. The gamma' relaxation is related to the molecular motion of absorbed water.
引用
收藏
页码：713 / 721
页数：9
相关论文
共 50 条
  • [1] BASE HYDROLYSIS OF POLY[BIS(TRIFLUOROETHOXY)PHOSPHAZENE]
    FERRAR, W
    LENHART, W
    LIPPERT, J
    MOLAIRE, T
    GUISTINA, R
    BROWN, D
    PHOSPHORUS SULFUR AND SILICON AND THE RELATED ELEMENTS, 1989, 41 (1-2): : 147 - 153
  • [2] Sorption and diffusion of organic vapors in poly[bis(trifluoroethoxy)phosphazene] and poly [bis(phenoxy)phosphazene] membranes
    Department of Chemical Engineering, Yuan-Ze Institute of Technology, Chung-Li, Taoyuan, 320, Taiwan
    J. MEMBR. SCI., 1 (117-126):
  • [3] Blood compatibility of poly[bis(trifluoroethoxy)phosphazene]
    Grunze, M
    Welle, A
    Tur, D
    CONFERENCE PROCEEDINGS AT ANTEC '98: PLASTICS ON MY MIND, VOLS I-3: VOL I; PROCESSING, VOL II; SPECIAL AREAS, VOL III; MATERIALS, 1998, 44 : 2713 - 2717
  • [4] Gas transport in poly[bis(trifluoroethoxy)phosphazene]
    Hirose, Takuji, 1600, (38):
  • [5] The synthesis of poly[bis(trifluoroethoxy)phosphazene] nanofibers
    Chen, Da-Kai
    Qiu, Di-Hong
    Lu, Yin
    An, Quan-Fu
    Ge, Dan
    Liang, Huan
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2008, 24 (12): : 58 - 61
  • [6] Sorption and diffusion of organic vapors in poly[bis(trifluoroethoxy) phosphazene] and poly[bis(phenoxy)phosphazene] membranes
    Sun, YM
    Lin, CL
    Chen, YK
    Wu, CH
    JOURNAL OF MEMBRANE SCIENCE, 1997, 134 (01) : 117 - 126
  • [7] THERMAL-PROPERTIES OF POLY-BIS-(TRIFLUOROETHOXY)PHOSPHAZENE
    KALASHNIK, AT
    RUDINSKAYA, GY
    PAPKOV, SP
    GOLOVA, LK
    KRUCHININ, NP
    VASILEVA, NV
    TUR, DR
    VYSOKOMOLEKULYARNYE SOEDINENIYA SERIYA A, 1990, 32 (05): : 1053 - 1057
  • [8] RHEOLOGICAL PROPERTIES OF POLY-BIS-(TRIFLUOROETHOXY) PHOSPHAZENE SOLUTIONS
    VASILEVA, NV
    KULICHIKHIN, VG
    GOLOVA, LK
    TUR, DR
    VINOGRADOVA, SV
    PAPKOV, SP
    VYSOKOMOLEKULYARNYE SOEDINENIYA SERIYA A, 1989, 31 (04): : 852 - 858
  • [9] SPHERULITIC CRYSTALLIZATION IN POLY(BIS(TRIFLUOROETHOXY)PHOSPHAZENE), PBFP
    KOJIMA, M
    MAGILL, JH
    POLYMER, 1985, 26 (13) : 1971 - 1978
  • [10] Characteristics of phase transitions in poly[bis(trifluoroethoxy)phosphazene]
    Kalashnik, AT
    Papkov, SP
    Tur, DR
    FIBRE CHEMISTRY, 1998, 30 (05) : 308 - 311
12345