PROPERTIES OF CEMENT MORTARS REINFORCED WITH POLYPROPYLENE FIBERS

被引：0
|
作者：
Oktay, Didem [1 ]
Aktuerk, Buesra [1 ]
Kabay, Nihat [1 ]
机构：
[1] Yildiz Tech Univ, Dept Civil Engn, Construct Mat Div, Istanbul, Turkey
来源：
SIGMA JOURNAL OF ENGINEERING AND NATURAL SCIENCES-SIGMA MUHENDISLIK VE FEN BILIMLERI DERGISI | 2014年 / 32卷 / 02期
关键词：
Polypropylene fiber; mechanical properties; workability; drying shrinkage; pore ratio;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this paper, the effect of polypropylene fibers (PF) on fresh and hardened properties of cement mortars produced with white cement is reported. Nine mixtures were prepared by using different volume fractions and different sizes of PF from 0 to 1.5% and 6 and 12 mm, respectively. Water to cement and sand to cement ratio by weight was kept constant as 0.4 and 3.0, respectively. PF with different length and amounts was introduced to mixtures and its effect on workability, density, water absorption, compressive strength, flexural strength and drying shrinkage were determined. Pore ratio at the cross-section of the specimens was calculated by image analysis. Test results showed that the addition of PF in higher amounts decreased workability, fresh and hardened density, compressive and flexural strength and increased water absorption and pore ratio of the mixtures. However when used in lower amounts, PF improved drying shrinkage and flexural strength.
引用
收藏
页码：164 / 175
页数：12
相关论文
共 50 条
  • [1] Thermal effects on the mechanical properties of cement mortars reinforced with aramid, glass, basalt and polypropylene fibers
    Mazloom, Moosa
    Mirzamohammadi, Sajjad
    [J]. ADVANCES IN MATERIALS RESEARCH-AN INTERNATIONAL JOURNAL, 2019, 8 (02): : 137 - 154
  • [2] Mechanical Properties of Cement Mortars Reinforced with Polypropylene Fibers Subjected to High Temperatures and Different Cooling Regimes
    Alvarez, Yorly
    Prieto, Maria Isabel
    Cobo, Alfonso
    [J]. BUILDINGS, 2023, 13 (06)
  • [3] Properties of Clay Soil and Soil Cement Reinforced with Polypropylene Fibers
    Estabragh, A. R.
    Ranjbari, S.
    Javadi, A. A.
    [J]. ACI MATERIALS JOURNAL, 2017, 114 (02) : 195 - 205
  • [4] Preparation and Properties of Alkali Activated Foam Cement Reinforced with Polypropylene Fibers
    王立久
    谭晓倩
    [J]. Journal of Wuhan University of Technology(Materials Science), 2011, (05) : 960 - 964
  • [5] Preparation and Properties of Alkali Activated Foam Cement Reinforced with Polypropylene Fibers
    Wang Lijiu
    Tan Xiaoqian
    [J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2011, 26 (05): : 960 - 964
  • [6] Preparation and properties of alkali activated foam cement reinforced with polypropylene fibers
    Lijiu Wang
    Xiaoqian Tan
    [J]. Journal of Wuhan University of Technology-Mater. Sci. Ed, 2011, 26 : 960 - 964
  • [7] Behaviour of alkaline cement mortars reinforced with acrylic and polypropylene fibres
    Puertas, F
    Amat, T
    Vázquez, T
    [J]. MATERIALES DE CONSTRUCCION, 2000, 50 (259) : 69 - 84
  • [8] Mechanical and durable behaviour of alkaline cement mortars reinforced with polypropylene fibres
    Puertas, F
    Amat, T
    Fernández-Jiménez, A
    Vázquez, T
    [J]. CEMENT AND CONCRETE RESEARCH, 2003, 33 (12) : 2031 - 2036
  • [9] Microstructure of a cement matrix composite reinforced with polypropylene fibers
    Rincón, JM
    Romero, M
    Hernández-Crespo, M
    Talero, R
    García Santos, A
    [J]. MATERIALES DE CONSTRUCCION, 2004, 54 (274) : 73 - 82
  • [10] Properties of cementitious mortars reinforced with natural fibers
    Achour, Abderraouf
    Ghomari, Fouad
    Belayachi, Naima
    [J]. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2017, 31 (17) : 1938 - 1962
12345