SIMULATION OF THE CRACK TIP CHEMISTRY OF STRESS-CORROSION CRACKS IN 7XXX ALUMINUM POWDER ALLOYS

被引：4

作者：

LANGAN, TJ ^{[1
]}

CHRISTODOULOU, L ^{[1
]}

VENABLES, D ^{[1
]}

GREEN, JAS ^{[1
]}

PICKENS, JR ^{[1
]}

机构：

[1] UNIV FLORIDA,GAINESVILLE,FL 32601

来源：

CORROSION | 1988年 / 44卷 / 03期

关键词：

CORROSION - Stress Corrosion Cracking - Powder metal products;

D O I：

10.5006/1.3583920

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

An investigation into the pH changes of a simulated crack tip solution during stress corrosion of rapidly solidified powder metallurgy (PM) AlZnMgCuCo alloys has shown that a steady-state value of between 3. 7 and 4. 0 is attained. The rate of attaining this value is dependent on the Co, Zn, and Cu contents of the alloys and is controlled by the kinetics of hydrogen recombination and evolution. Cobalt exists in intermetallic Co//2Al//9 particles, which serve as the cathodic sites. It is shown that differences in stress corrosion behavior between the PM and the conventional AlZnMgCu alloys are not related to differences in the steady-state crack tip pH.

引用

页码：165 / 169

页数：5

共 50 条

[1] A HEAT-TREATMENT FOR REDUCING CORROSION AND STRESS-CORROSION CRACKING SUSCEPTIBILITIES IN 7XXX ALUMINUM-ALLOYS
THOMPSON, JJ
TANKINS, ES
AGARWALA, VS
MATERIALS PERFORMANCE, 1987, 26 (06) : 45 - 52
[2] Stress corrosion cracking behaviour of 7xxx aluminum alloys: A literature review
Rao, A. C. Umamaheshwer
Vasu, V.
Govindaraju, M.
Srinadh, K. V. Sai
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (06) : 1447 - 1471
[3] Exacerbated stress corrosion cracking in arc welds of 7xxx aluminum alloys
Borchers, T. E.
Seid, A.
Shafer, P.
Zhang, W.
WELDING IN THE WORLD, 2018, 62 (04) : 783 - 792
[4] The influence of microstructure on the formation of stress corrosion cracks in 7XXX series aluminium alloys
Deshais, G
Newcomb, SB
ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 1635 - 1640
[5] Influence of microstructure on the formation of stress corrosion cracks in 7XXX series aluminium alloys
Deshais, G.
Newcomb, S.B.
Materials Science Forum, 2000, 331
[6] Study of the crack sensitivity of 6xxx and 7xxx aluminum alloys
Nagaumi, H
Takateru, U
THERMEC'2003, PTS 1-5, 2003, 426-4 : 465 - 470
[7] A statistical model for localized corrosion in 7xxx aluminum alloys
Huang, T-S.
Zhao, S.
Frankel, G. S.
Wolfe, D. A.
CORROSION, 2007, 63 (09) : 819 - 827
[8] SEPARATION OF MECHANICAL AND ELECTROCHEMICAL ASPECTS OF STRESS-CORROSION CRACKING OF HIGH-STRENGTH ALUMINUM I 7XXX ALLOYS
STARKE, EA
STALEY, JT
HOLLINGSWORTH, EH
CORROSION, 1977, 33 (04) : 150 - 150
[9] STRESS-CORROSION CRACKING EVALUATION OF HIGH-STRENGTH 7XXX P/M ALLOYS
HAFEEZ, A
HILDEMAN, GJ
BROWNHILL, DJ
LABARRE, LC
JOURNAL OF METALS, 1983, 35 (12): : 62 - 62
[10] INITIATION OF STRESS-CORROSION CRACKS IN ALUMINUM-ALLOYS
PATHANIA, RS
TROMANS, D
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (04): : 607 - 612

← 1 2 3 4 5 →