CONTROL OF RECRYSTALLIZATION DURING HIGH-TEMPERATURE HOT-ROLLING OF GRAIN-ORIENTED SILICON STEEL

被引：15
|
作者：
MURAKI, M
OBARA, T
SATOH, M
KAN, T
机构：
[1] Iron and Steel Research Laboratories, Kawasaki Steel Corporation, Kurashiki
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 1995年 / 4卷 / 04期
关键词：
HOT ROLLING; RECRYSTALLIZATION; SILICON STEELS;
D O I：
10.1007/BF02649300
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Recrystallization kinetics of 3% Si steel after hot rolling in the temperatures between 1373 and 1573 K, which is quite important to obtain uniform magnetic properties, was studied, Recrystallization rate after hot rolling was relatively slow because of low dislocation density, which resulted from rapid recovery, and its behavior was strongly influenced by the initial grain size and coexistence of the gamma phase. Based on these findings, controlling technology of recrystallization during hot rolling of grain-oriented Si steels is discussed.
引用
收藏
页码：413 / 417
页数：5
相关论文
共 50 条
  • [1] Development of high-temperature hot-rolling process for grain-oriented silicon steel
    Muraki, M
    Ozaki, Y
    Obara, T
    Kan, T
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1996, 5 (03) : 323 - 327
  • [2] KINETICS OF SECONDARY RECRYSTALLIZATION IN GRAIN-ORIENTED SILICON STEEL STUDIED BY HIGH-TEMPERATURE BACKGROUND
    IWASAKI, Y
    FUJIMOTO, K
    [J]. JOURNAL DE PHYSIQUE, 1981, 42 (NC5): : 493 - 498
  • [3] Secondary recrystallization in grain-oriented silicon steel
    Ushigami, Y
    Kumano, T
    Haratani, T
    Nakamura, S
    Takebayashi, S
    Kubota, T
    [J]. RECRYSTALLIZATION AND GRAIN GROWTH, PTS 1 AND 2, 2004, 467-470 : 853 - 862
  • [4] The Influence of Hot Rolling Technological Parameters on Microstructure of Low Temperature Grain-Oriented Silicon Steel
    Feng, Yunli
    Qi, Xuejing
    Song, Meng
    [J]. ADVANCES IN CHEMICAL ENGINEERING, PTS 1-3, 2012, 396-398 : 1841 - 1845
  • [5] STABILITY OF SECONDARY RECRYSTALLIZATION IN GRAIN-ORIENTED SILICON STEEL
    Namba, Eiichi
    Arai, Satoshi
    Homma, Hotaka
    Ushigami, Yoshiyuki
    [J]. MATERIALS PROCESSING AND TEXTURE, 2009, 200 : 275 - 284
  • [6] Hot Rolling Twinning Behavior of Strip Casting Grain-Oriented Silicon Steel
    Song H.-Y.
    Liu H.-T.
    Wang G.-D.
    [J]. Dongbei Daxue Xuebao/Journal of Northeastern University, 2022, 43 (02): : 182 - 187
  • [7] TEXTURE CHANGES DURING SECONDARY RECRYSTALLIZATION OF A HIGH-PERMEABILITY GRAIN-ORIENTED SILICON STEEL
    FLOWERS, JW
    [J]. JOURNAL OF APPLIED PHYSICS, 1982, 53 (11) : 8305 - 8307
  • [8] GRAIN-REFINEMENT OF NB STEELS BY CONTROL OF RECRYSTALLIZATION DURING HOT-ROLLING
    CUDDY, LJ
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (01): : 87 - 98
  • [9] Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
    Xu Zhanyi
    Sha Yuhui
    Zhang Fang
    Zhang Huabing
    Li Guobao
    Chu Shuangjie
    Zuo Liang
    [J]. ACTA METALLURGICA SINICA, 2020, 56 (08) : 1067 - 1074
  • [10] Orientation Selectivity of Secondary Recrystallization In Grain-Oriented Silicon Steel
    Ushigami, Yoshiyuki
    Arira, Yoshihiro
    Ushioda, Kohsaku
    [J]. RECRYSTALLIZATION AND GRAIN GROWTH V, 2013, 753 : 337 - +
12345