STRESS-CORROSION CRACKING OF ANNEALED AND SENSITIZED TYPE-304 STAINLESS-STEEL IN DEAERATED CHLORIDE-SULFATE SOLUTIONS AT 290 C

被引：7

作者：

POZNANSKY, A ^{[1
]}

DUQUETTE, DJ ^{[1
]}

机构：

[1] RENSSELAER POLYTECH INST,TROY,NY 12181

来源：

CORROSION | 1983年 / 39卷 / 11期

关键词：

D O I：

10.5006/1.3581902

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

引用

页码：425 / 431

页数：7

共 50 条

[1] STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN THIOCYANATE SOLUTIONS
PERILLO, PM
DUFFO, GS
[J]. CORROSION, 1990, 46 (07) : 545 - 546
[2] STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN THIOSULFATE SOLUTIONS
NEWMAN, RC
SIERADZKI, K
ISAACS, HS
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (11): : 2015 - 2026
[3] STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN HIGH-TEMPERATURE CHLORIDE SOLUTIONS
LIN, LF
CRAGNOLINO, G
SZKLARSKASMIALOWSKA, Z
MACDONALD, DD
[J]. CORROSION, 1981, 37 (11) : 616 - 627
[4] POTENTIAL AND CHLORIDE EFFECTS IN STRESS-CORROSION CRACKING OF TYPE-304 STAINLESS-STEEL IN 290C WATER
JONES, RL
[J]. CORROSION, 1975, 31 (12) : 424 - 431
[5] STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN SULFATE AND CHLORIDE SOLUTIONS AT 250-DEGREES-C AND 100-DEGREES-C
CRAGNOLINO, G
LIN, LF
SZKLARSKASMIALOWSKA, Z
[J]. CORROSION, 1981, 37 (06) : 312 - 320
[6] THE AMOUNT OF CHLORINE CONTAMINATION FOR PREVENTION OF STRESS-CORROSION CRACKING IN SENSITIZED TYPE-304 STAINLESS-STEEL
TOKIWAI, M
KIMURA, H
KUSANAGI, H
[J]. CORROSION SCIENCE, 1985, 25 (8-9) : 837 - 844
[7] INITIATION OF STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN DILUTE THIOSULFATE SOLUTION
ISAACS, HS
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1988, 135 (09) : 2180 - 2183
[8] INITIATION OF STRESS-CORROSION CRACKING OF SENSITIZED TYPE 304 STAINLESS-STEEL
ISAACS, HS
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1986, 133 (08) : C303 - C303
[9] INTERGRANULAR STRESS-CORROSION CRACKING OF SENSITIZED TYPE-304 STAINLESS-STEEL IN SODIUM-SULFATE AT APPROXIMATELY 100-DEGREES-C
TANNO, K
YASHIRO, H
KAWAMURA, Y
UMEGAI, K
KUMAGAI, N
[J]. CORROSION, 1993, 49 (04) : 319 - 326
[10] EFFECT ON SPECIMEN WIDTH ON STRESS-CORROSION CRACKING OF TYPE-304 STAINLESS-STEEL
NISHIMURA, R
[J]. CORROSION, 1993, 49 (10) : 796 - 801

← 1 2 3 4 5 →