PVD HARD COATINGS ON PRENITRIDED LOW-ALLOY STEEL

The combination of traditional surface treatments such as nitriding with modem plasma-enhanced surface technologies reveals the possibility, particularly in the application to low alloy steels, of obtaining mechanical properties comparable with those of high alloy steels. Gas-nitrided samples of the hardened and tempered low alloy steels 30CrMoV9 and 17CrMoV10 were TiN coated by r.f. magnetron sputtering and ion plating. The requirements to obtain a nitrided substrate that can be coated were given special consideration. For this, various surface modifications of the nitrided substrates were realized by bright nitriding, nitriding with a compound layer and additional steps before coating, such as polishing, grinding and sputter cleaning. The properties of prenitrided coated steels essentially depend on the structure and properties of the outer part of the nitrided case. TiN on bright nitrided and nitrided substrates with the compound layer removed has a better adherence than on compound layers. The decomposition of the iron nitride during the plasma sputter cleaning of compound layers results in a lower surface hardness and lower adherence of TiN. The highest wear resistances in the Timken test were registered on samples where the compound layer had been removed before TiN coating.