Al-Zn-Mg-Cu Alloys with Strength of 800MPa

被引：9

作者：

Yang Shou-jie ^{[1
,2
]}

Xing Qing-yuan ^{[1
,2
]}

Yu Hai-jun ^{[1
,2
]}

Wang Yu-ling ^{[1
,2
]}

Dai Sheng-long ^{[1
,2
]}

机构：

[1] AECC Beijing Inst Aeronaut Mat, Beijing 100095, Peoples R China

[2] Beijing Engn Technol Res Ctr Adv Aluminum Mat & A, Beijing 100095, Peoples R China

来源：

CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING | 2018年 / 46卷 / 04期

关键词：

ultra-high strength Al alloy; DC casting; RRA heat treatment; mechanical property;

D O I：

10.11868/j.issn.1001-4381.2017.000277

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This research has produced Al-Zn-Mg-Cu alloy containing 20%(mass fraction, the same below) alloying elements by the Hot-top semi-continuous DC casting equipment, which has adopted purifying and refining on-line technologies. This alloy has broken the limit of 7000 Al-alloy containing no more than 14% alloying elements. The microstructure and fracture of the alloy were investigated by optical microscopy (OM) , transmission electron microscopy (TEM) and scanning electron microscopy (SEM) , the temperature of phases transformation was investigated by differential scanning calorimetry (DSC), and the hardness and tensile properties were also tested. The tensile strength, yield strength and elongation of this alloy can be up to 810.3, 799. 3MPa and 3. 4.% by RRA heat-treatment after extrusion. Through the study on the single and tertiary-stage ageing treatment kinetics, the optimum ageing temperature 120 degrees C is identified and a wider range of aging time can be chosen. Moreover, no other precipitates are found in the alloy containing 16. 1%Zn element, and the joint strengthening comes from the undissolved second phase and the ageing precipitation eta' phase.

引用

页码：82 / 90

页数：9

共 26 条

[1] Dai Xiao-yuan, 2007, Chinese Journal of Nonferrous Metals, V17, P396
[2] Precipitate characterisation in metallic systems by small-angle X-ray or neutron scattering
De Geuser, Frederic
Deschamps, Alexis
[J]. COMPTES RENDUS PHYSIQUE, 2012, 13 (03) : 246 - 256
[3] Quantitative Characterization of Precipitate Microstructures in Metallic Alloys Using Small-Angle Scattering
Deschamps, Alexis
De Geuser, Frederic
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (01): : 77 - 86
[4] Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys
Dixit, M.
Mishra, R. S.
Sankaran, K. K.
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2): : 163 - 172
[5] Recent development in aluminium alloys for aerospace applications
Heinz, A
Haszler, A
Keidel, C
Moldenhauer, S
Benedictus, R
Miller, WS
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 280 (01): : 102 - 107
[6] Microstructure of a rapidly solidified Al-4V-2Fe ultrahigh strength aluminum alloy
Hono, K
Zhang, Y
Sakurai, T
Inoue, A
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 250 (01): : 152 - 157
[7] High-strength aluminum- and zirconium-based alloys containing nanoquasicrystalline particles
Inoue, A
Kimura, HM
Zhang, T
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 294 : 727 - 735
[8] High-strength aluminum alloys containing nanoquasicrystalline particles
Inoue, A
Kimura, H
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 286 (01): : 1 - 10
[9] Inoue A., 2001, J LIGHT MET, V1, P31, DOI [DOI 10.1016/S1471-5317(00)00004-3, 10.1016/S1471-5317(00)00004-3]
[10] Correlations between intergranular stress corrosion cracking, grain-boundary microchemistry, and grain-boundary electrochemistry for Al-Zn-Mg-Cu alloys
Knight, S. P.
Birbilis, N.
Muddle, B. C.
Trueman, A. R.
Lynch, S. P.
[J]. CORROSION SCIENCE, 2010, 52 (12) : 4073 - 4080

← 1 2 3 →