SINTERING CONDITION AND CHARACTERISTICS OF NIO-MGO SOLID-SOLUTION

被引：0

作者：

TAKAHASHI, K ^{[1
]}

ASADA, M ^{[1
]}

KAWAKAMI, M ^{[1
]}

机构：

[1] TOYOHASHI UNIV TECHNOL,TOYOHASHI,AICHI 440,JAPAN

来源：

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1993年 / 79卷 / 05期

关键词：

NICKEL OXIDE; MAGNESIA; SOLID SOLUTION; POROSITY; SURFACE AREA; GRAIN SIZE; BULK DIFFUSION; SINTERING MECHANISM;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effects of the temperature and MgO content on the sintering characteristics of NiO were investigated by measuring the porosity, the specific surface area and the gran size. NiO compacts containing 0 to 20mol%MgO were sintered over the temperature range 1273 to 1773K in air. The results were summarized as follows. 1) The sintering proceeded remarkably at higher temperature than 1473K. 2) Both of the prosity and the specific surface area decreased with increasing the temperature and MgO content. The effect of MgO addition on the decrease in the specific surface area was more significant than that on the decrease in the porosity. 3) Grain growth was expressed as 1/3 power function of time. The addition of MgO accelerated both the grain growth and the closed pore formation. 4) Sintering mechanism was explained by bulk diffusion of oxygen ion. 5) Lattice constant increased linearly with MgO

引用

页码：19 / 24

页数：6

共 50 条

[1] EFFECTS OF MGO CONTENT AND TEMPERATURE ON THE REDUCTION RATE OF NIO-MGO SOLID-SOLUTION BY HYDROGEN
TAKAHASHI, K
ASADA, M
KAWAKAMI, M
[J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1994, 80 (02): : 95 - 100
[2] FORMATION OF POROUS NICKEL IN THE REDUCTION OF NIO-MGO SOLID-SOLUTION DOPED WITH FEO
IGUCHI, Y
HIRAO, J
[J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1984, 48 (08) : 802 - 807
[3] KINETICS OF ORDERING IN A NIO-MGO SOLID SOLUTION
CHUDINOVA, SA
KUZKINA, SP
SHIVRIN, ON
[J]. SOVIET PHYSICS SOLID STATE,USSR, 1970, 11 (08): : 1917 - +
[4] THERMODYNAMIC ACTIVITIES OF NIO IN NIO-MGO SOLID SOLUTIONS
SEETHARAMAN, S
ABRAHAM, KP
[J]. INDIAN JOURNAL OF TECHNOLOGY, 1968, 6 (04): : 123 - +
[5] Development of NiO-MgO solid solution catalyst for natural gas reforming under pressurized condition.
Fujimoto, K
Tomishige, K
Himeno, Y
Matsuo, Y
[J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2000, 219 : U253 - U253
[6] MAGNETIC PROPERTIES OF NIO-MGO SOLID SOLUTIONS
ARIYA, SM
LUKINYKH, NL
[J]. SOVIET PHYSICS SOLID STATE,USSR, 1966, 8 (01): : 210 - +
[7] SEGREGATION IN NIO-MGO SOLID-SOLUTIONS
KLUZ, Z
STOCH, J
CZEPPE, T
[J]. ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-WIESBADEN, 1983, 134 (1-2): : 125 - 127
[8] Energy efficient conversion of methane to syngas over NiO-MgO solid solution
Choudhary, VR
Mamman, AS
[J]. APPLIED ENERGY, 2000, 66 (02) : 161 - 175
[9] CHARACTERISTICS OF DIFFUSION COUPLES FE-MGO AND NIO-MGO
BLANK, SL
PASK, JA
[J]. AMERICAN CERAMIC SOCIETY BULLETIN, 1965, 44 (09): : 731 - &
[10] Dry reforming of methane to synthesis gas on NiO-MgO nanocrystalline solid solution catalysts
Zanganeh, Rasoul
Rezaei, Mehran
Zamaniyan, Akbar
[J]. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2013, 38 (07) : 3012 - 3018

← 1 2 3 4 5 →