Kinetics of the Low-temperature Pyrolysis of Mixed Plastics in the Batch Reactor

Pyrolytic characteristics of mixed plastics containing 22 wt.% HDPE, 17 wt.% LDPE, 27 wt.% PP, 12 wt.% PS, 16 wt.% ABS, 6 wt.% PVC have been studied in the batch-type microreactor of stainless steel. Thermal degradation experiments were performed at temperature of 410 similar to 450 degrees C. The yield of each pyrolytic products were obtained by the weight measurement and molecular weight distribution of pyrolytic liquid products determined by the GC-SIMDIS method. It was shown that the yield and molecular weight of pyrolytic liquid product were decreased with the increase of reaction temperature and time. It was know that 20wt% of PVC composing of the mixed plastics was converted to the gas products of chloride during the pyrolysis process. The chain-end scission rate parameter was determined to be 50.2 kcal/mole of mixed plastics by the Arrhenius plot.