Radiation-Induced Change in the Properties of Isotropic Structural Graphite

Three types of samples of isotropic graphite with different grain density and size were irradiated in a BOR-60 reactor up to neutron fluence (1.7–2.8)·1026 m–2 (E > 0.18 MeV) at 360–400°C. After irradiation, the change in the dimensions, resistivity, linear thermal expansion coefficient and dynamic elastic modulus were investigated. It was determined that the density in the range 1.67–1.76 g/cm3 results in an increase of the maximum weight and depth of volume shrinkage of isotropic fine-grain graphite. An equation was proposed for fitting the temperature dependence of the critical neutron fluence in the range 380–780°C for the experimental graphite samples.