Study on electrochemical performance of Mg-doped Li2FeSiO4 cathode material for Li-ion batteries

In this paper, Li2Fe1−yMgySiO4/C (y = 0, 0.01, 0.02, 0.03, 0.05), a cathode material for lithium-ion battery was synthesized by solid-state method and modified by doping Mg2+ on the iron site. The effects of Mg2+ doping on the crystal structure and electrochemical performance Li2FeSiO4 was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and electrochemical tests. Electrochemical methods of measurement were applied including constant current charge–discharge test, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS), to determine the electrochemical performance of the material and the optimal doping ion and ratio. The results showed that Li2Fe0.98Mg0.02SiO4/C has the higher specific capacity and better cycle stability as well as lower impedance and better reversibility. The enhanced electrochemical performance can be attributed to the increased electronic conductivity, the decreased charge transfer impedance, and the improved Li-ion diffusion coefficient. Then, further study on the synthesis conditions was performed to find the optimal combustion temperature and time. According to the study, the material which has the best electrochemical performance, shows initial discharge specific capacity of 142.3 mAh g−1 at 0.1 C (1 C = 166 mA g−1) and coulomb efficiency of 95.6%, under the condition that the temperature is 700 °C and the calcining time is 10 h.