Interaction of Exogenous Aluminum Oxide Nanophases with Tin and Antimony in Cobalt Melts. II. Surface Tension and Density

被引：0
|
作者：
S. N. Anuchkin
V. T. Burtsev
A. V. Samokhin
机构：
[1] Baikov Institute of Metallurgy and Materials Science,
[2] Russian Academy of Sciences,undefined
来源：
Russian Metallurgy (Metally) | 2023年 / 2023卷
关键词：
exogenous nanoparticles; aluminum oxide; nonferrous metal impurities; cobalt-based melts; tin; antimony; surface tension; density;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：54 / 61
页数：7
相关论文
共 6 条
  • [1] Interaction of Exogenous Aluminum Oxide Nanophases with Tin and Antimony in Cobalt Melts. II. Surface Tension and Density1
    Anuchkin, S. N.
    Burtsev, V. T.
    Samokhin, A. V.
    RUSSIAN METALLURGY, 2023, 2023 (01): : 54 - 61
  • [2] Interaction of Exogenous Aluminum Oxide Nanophases with Tin and Antimony in Cobalt Melts. I. Heterophase Interaction
    Anuchkin, S. N.
    Burtsev, V. T.
    Samokhin, A., V
    RUSSIAN METALLURGY, 2022, 2022 (09): : 1043 - 1049
  • [3] Interaction of Exogenous Aluminum Oxide Nanophases with Tin and Antimony in Cobalt Melts. I. Heterophase Interaction
    S. N. Anuchkin
    V. T. Burtsev
    A. V. Samokhin
    Russian Metallurgy (Metally), 2022, 2022 : 1043 - 1049
  • [4] Interaction of exogenous zirconium oxide nanophases with sulfur and tin in nickel melts
    Anuchkin S.N.
    Burtsev V.T.
    Samokhin A.V.
    Burtsev, V.T. (burtsev@ultra.imet.ac.ru), 1600, Izdatel'stvo Nauka (2016): : 1042 - 1048
  • [5] Investigation into the Interaction of Exogenous Refractory Nanophases with a Fe-C-Si Melt (Cast Iron) at 1350 degrees C: II. Effect of Nanophases on Surface Tension, Density of Melt, and Mechanical Properties of Metal
    Burtsev, V. T.
    Anuchkin, S. N.
    Samokhin, A. V.
    NANOTECHNOLOGIES IN RUSSIA, 2018, 13 (11-12): : 594 - 601
  • [6] Interaction of refractory compound nanoparticles with a surfactant in a nickel melt: II. Surface tension and density
    Anuchkin S.N.
    Burtsev V.T.
    Samokhin A.V.
    Russian Metallurgy (Metally), 2011, 2011 (3) : 180 - 184
1