Wear behavior of as-deposited and oxidized ternary (Zr,Hf)N coatings

被引：0
|
作者：
Erdem Atar
E. Sabrikayali
Huseyin Cimenoglu
机构：
[1] Gebze Institute of Technology,the Materials Science and Engineering Department
[2] Istanbul Technical University,the Department of Metallurgy and Materials Engineering
来源：
Metallurgical and Materials Transactions A | 2005年 / 36卷
关键词：
Material Transaction; Wear Resistance; Mass Gain; Wear Track; Wear Scar;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In the present study, the tribological performance of ternary (Zr,Hf)N coatings, whose Hf content was varied between 0 and 21 wt pct, has been systematically examined in the as-deposited and oxidized conditions. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400 °C for times up to 12 hours in air. Wear tests revealed pronounced improvement in the wear resistance with increasing Hf content in the as-deposited coatings. Oxidation for 12 hours yielded more than a fourfold increase in wear resistance. The beneficial effect of Hf on wear resistance decreased upon oxidation.
引用
收藏
页码：2793 / 2800
页数：7
相关论文
共 50 条
  • [1] Wear behavior of As-deposited and oxidized ternary (Zr,Hf)N coatings
    Atar, E
    Kayali, ES
    Cimenoglu, H
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (10): : 2793 - 2800
  • [2] Reciprocating wear behaviour of (Zr, Hf)N coatings
    Atar, E
    Kayali, ES
    Cimenoglu, H
    WEAR, 2004, 257 (5-6) : 633 - 639
  • [3] Fretting wear of ZrN and Zr(21% Hf)N coatings
    Atar, E
    Çimenoglu, H
    Kayali, ES
    EURO CERAMICS VIII, PTS 1-3, 2004, 264-268 : 477 - 480
  • [4] INVESTIGATION OF Zr-ZrN, Zr,Hf-(Zr,Hf)N AND Zr,Nb-(Zr,Nb)N COATINGS DEPOSITED ON A TITANIUM ALLOY SUBSTRATE
    Vereschaka, Alexey
    Sotova, Catherine
    Milovich, Filipp
    Bublikov, Jury
    Zhylinski, Valery
    Makarevich, Kirill
    Baranova, Natalia
    HIGH TEMPERATURE MATERIAL PROCESSES, 2024, 28 (02): : 65 - 80
  • [5] Sliding wear behaviour of ZrN and (Zr, 12 wt% Hf)N coatings
    Atar, E
    Kayali, ES
    Cimenoglu, H
    TRIBOLOGY INTERNATIONAL, 2006, 39 (04) : 297 - 302
  • [6] Investigations of the Deuterium Permeability of As-Deposited and Oxidized Ti2AlN Coatings
    Groener, Lukas
    Mengis, Lukas
    Galetz, Mathias
    Kirste, Lutz
    Daum, Philipp
    Wirth, Marco
    Meyer, Frank
    Fromm, Alexander
    Blug, Bernhard
    Burmeister, Frank
    MATERIALS, 2020, 13 (09)
  • [7] A comparison of the wear life of as-deposited and ion-irradiated WS2 coatings
    Rai, AK
    Bhattacharya, RS
    Zabinski, JS
    Miyoshi, K
    SURFACE & COATINGS TECHNOLOGY, 1997, 92 (1-2): : 120 - 128
  • [8] Influence of the tribological properties of the Zr,Hf-(Zr,Hf)N-(Zr,Me,Hf,Al) N coatings (where Me is Mo, Ti, or Cr) with a nanostructured wear-resistant layer on their wear pattern during turning of steel
    Grigoriev, Sergey
    Vereschaka, Alexey
    Uglov, Vladimir
    Milovich, Filipp
    Tabakov, Vladimir
    Cherenda, Nikolai
    Andreev, Nikolay
    Migranov, Mars
    WEAR, 2023, 518
  • [9] Hardness characterisation of thin Zr(Hf,N) coatings
    Atar, E
    Çimenoglu, H
    Kayali, ES
    SURFACE & COATINGS TECHNOLOGY, 2003, 162 (2-3): : 167 - 173
  • [10] Sliding wear of as-deposited and heat-treated nanocrystalline nickel-tungsten alloy coatings
    Vamsi, M. V. N.
    Wasekar, Nitin P.
    Sundararajan, G.
    WEAR, 2018, 412 : 136 - 143
12345