Inhibition of Aluminum Alloy Corrosion in 0.5 M Nitric Acid Solution by 4-4-Dimethyloxazolidine-2-thione

The corrosion inhibition of Al-Alloy (Al2024) in 0.5 M nitric acid solution at 30 °C was achieved using 4-4-dimethyloxazolidine-2-thione (DMT) as a corrosion inhibitor. The electrochemical performance of the DMT was studied by electrochemical impedance spectroscopy (EIS), potentiodynamic polarization measurements, and scanning electron microscopic study (SEM). The results indicated that DMT acts as an inhibitor for Al2024 in 0.5 M nitric acid. Polarization curves indicated that DMT was a mixed-type inhibitor. Inhibition efficiencies were observed to be increased with an increase in DMT concentration and attains approximately to 93.4% at 2 mM of DMT in 0.5 M nitric acid. The adsorption of DMT model on Al2024 surface obeyed in accordance with Langmuir adsorption isotherm model. The value of the free energy of adsorption ΔGads indicated that the adsorption of DMT molecule was a spontaneous process and was typical of physical and chemical adsorption.