Influence of high-temperature protective coatings on the mechanical properties of nickel-based superalloys

被引:0
|
作者
Y. Itoh
M. Saitoh
Y. Ishiwata
机构
[1] Toshiba Corporation,Power and Industrial Systems Research and Development Center
来源
关键词
Fatigue Crack; Fatigue Life; Plasma Spray Coating; Creep Life; MCrAlY Coating;
D O I
暂无
中图分类号
学科分类号
摘要
The low-pressure plasma spray coating process has been established in the field of gas turbines and is used for hot parts, such as turbine blades and duct segments, which are exposed to corrosive gases at high temperatures. Overlay coatings based on the MCrAlY alloy system (M is Ni, CO or both) are commonly employed as oxidation- and corrosion-resistant coatings. Mechanical properties, such as creep and fatigue lives, of various MCrAlY coating systems were investigated at high temperature as compared with the uncoated substrates, such as eqiaxis IN738LC, directional solidified CM247LC and single-crystal CMSX-2. It was clear that the MCrAlY coatings had no significant influence on the creep lives of substrates for the sake of superior ductility of MCrAlY coatings at high temperature. The low-cycle fatigue lives of MCrAlY coated superalloys at high temperature showed only a little superior performance in comparison with the uncoated results. However, the high-cycle fatigue lives of MCrAlY coated superalloys at high temperature showed inferior performance in comparison with the uncoated results. It was because that the low-cycle fatigue cracks initiated at casting cavities inside the substrate in both the coated and the noncoated cases. However, the high-cycle fatigue cracks initiated at interface defects, such as small pores and grit residues, between the MCrAlY coating and the substrate and grew into the MCrAlY coating, and then into the substrate.
引用
收藏
页码:3957 / 3966
页数:9
相关论文
共 50 条
  • [1] Influence of high-temperature protective coatings on the mechanical properties of nickel-based superalloys
    Itoh, Y
    Saitoh, M
    Ishiwata, Y
    [J]. JOURNAL OF MATERIALS SCIENCE, 1999, 34 (16) : 3957 - 3966
  • [2] Effect of high-temperature protective coatings on fatigue lives of nickel-based superalloys
    Itoh, Y
    Saitoh, M
    Takaki, K
    Fujiyama, K
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (12) : 843 - 854
  • [3] High-temperature mechanical properties of nickel-based superalloys manufactured by additive manufacturing
    GaoLe, Zhao
    Yun, Jiang
    XiaoAn, Hu
    Jia, Huang
    JinWu, Wu
    Yun, Wang
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 2020, 36 (14) : 1523 - 1533
  • [4] High-temperature protective coatings on superalloys
    Liu, PS
    Liang, KM
    Zhou, HY
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2002, 12 (04) : 798 - 803
  • [5] Thermal Barrier Coatings for High-Temperature Performance of Nickel-Based Superalloys: A Synthetic Review
    Barwinska, Izabela
    Kopec, Mateusz
    Kukla, Dominik
    Senderowski, Cezary
    Kowalewski, Zbigniew L. L.
    [J]. COATINGS, 2023, 13 (04)
  • [6] High-temperature protective coatings on superalloys
    刘培生
    梁开明
    周宏余
    [J]. Transactions of Nonferrous Metals Society of China, 2002, (04) : 798 - 803
  • [7] Influence of prestraining on the high-temperature fatigue behaviour of polycrystalline nickel-based superalloys in the VHCF range
    Stoecker, Christian
    Zimmermann, Martina
    Christ, Hans-Juergen
    [J]. FATIGUE 2010, 2010, 2 (01): : 1383 - 1392
  • [8] THE INFLUENCE OF GASEOUS IMPURITIES IN AIR ON THE HIGH-TEMPERATURE CORROSION OF COATED AND UNCOATED NICKEL-BASED SUPERALLOYS
    LINK, T
    RAHMEL, A
    SCHUTZE, M
    [J]. MATERIALS AT HIGH TEMPERATURES, 1995, 13 (01) : 55 - 66
  • [9] MICROSTRUCTURAL DEGRADATION OF ALUMINIDE COATINGS ON SINGLE-CRYSTAL NICKEL-BASED SUPERALLOYS DURING HIGH-TEMPERATURE EXPOSURE
    GALE, WF
    KING, JE
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 1993, 9 (09) : 793 - 798
  • [10] HIGH-TEMPERATURE THERMAL-DIFFUSIVITY OF NICKEL-BASED SUPERALLOYS AND INTERMETALLIC COMPOUNDS
    HAZOTTE, A
    PERROT, B
    ARCHAMBAULT, P
    [J]. JOURNAL DE PHYSIQUE IV, 1993, 3 (C7): : 351 - 354