Influence of phosphorus element on direct laser sintering of multicomponent Cu-based metal powder

被引:0
|
作者
D. D. Gu
Y. F. Shen
机构
[1] Nanjing University of Aeronautics and Astronautics,the College of Materials Science and Technology
关键词
Material Transaction; Liquid Phase Sinter; Powder System; Phosphorus Addition; Longitudinal Shrinkage;
D O I
暂无
中图分类号
学科分类号
摘要
This article presents a detailed investigation on the influence of the phosphorus element upon the laser sintering of a multicomponent Cu-based metal powder system consisting of Cu, Cu-10Sn, and Cu-8.4P. Powder systems containing 0, 10, 15, and 20 wt pct CuP were sintered in atmosphere at room temperature using the following optimal processing parameters: laser power of 350 W, scan speed of 0.04 m/s, scan line spacing of 0.15 mm, and layer thickness of 0.25 mm. It was found that the relative density of the sintered sample with 15 wt pct CuP increased by 24,4 pct as compared with the sample without phosphorus addition. A further increase in the CuP content (≥20 wt pct), however, resulted in a poor densification with a serious delamination. The exact metallurgical roles of the phosphorus element in the laser sintering process were addressed as follows. First, the phosphorus could prevent the sintering system from oxidation by forming CuPO3, thereby improving the wetting characteristics and the sintering kinetics. Second, the phosphorus could decrease the surface tension of molten materials, leading to a successive transition from highly discontinuous sintered tracks to fairly coherent ones with increasing the phosphorus content. Third, the phosphorus could lower the melt viscosity, thereby improving the microstructural homogeneity of the laser-sintered samples.
引用
收藏
页码:967 / 977
页数:10
相关论文
共 50 条
  • [1] Influence of phosphorus element on direct laser sintering of multicomponent Cu-based metal powder
    Gu, D. D.
    Shen, Y. F.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2006, 37 (06): : 967 - 977
  • [2] Development and characterisation of direct laser sintering Cu-based metal powder
    Zhu, HH
    Lu, L
    Fuh, JYH
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 140 : 314 - 317
  • [3] Microstructural evolution in direct laser sintering of Cu-based metal powder
    Zhu, HH
    Fuh, JYH
    Lu, L
    [J]. RAPID PROTOTYPING JOURNAL, 2005, 11 (02) : 74 - 81
  • [4] Effect of braze flux on direct laser sintering Cu-based metal powder
    Zhu, HH
    Lu, L
    Fuh, JYH
    Wu, CC
    [J]. MATERIALS & DESIGN, 2006, 27 (02) : 166 - 170
  • [5] Development and characterisation of direct laser sintering multicomponent Cu based metal powder
    Gu, D. D.
    Shen, Y. F.
    [J]. POWDER METALLURGY, 2006, 49 (03) : 258 - 264
  • [6] Effects of processing parameters on direct laser sintering of multicomponent Cu based metal powder
    Gu, D. D.
    Shen, Y. F.
    Yang, J. L.
    Wang, Y.
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 2006, 22 (12) : 1449 - 1455
  • [7] Direct laser sintering of Cu-based metal for rapid tooling
    Tang, Y.
    Loh, H. T.
    Fuh, J. Y. H.
    Wong, Y. S.
    Lu, L.
    [J]. INTERNATIONAL JOURNAL OF COMPUTER APPLICATIONS IN TECHNOLOGY, 2007, 28 (01) : 63 - 68
  • [8] Direct laser sintering of Cu-based metallic powder for injection moulding
    Zhu, HH
    Fuh, JYH
    Lu, L
    [J]. AMST 02: ADVANCED MANUFACTURING SYSTEMS AND TECHNOLOGY, PROCEEDINGS, 2002, (437): : 779 - 784
  • [9] Development a Cu-based Metal Powder for Selective Laser Micro Sintering
    Dai, C.
    Zhu, H. H.
    Ke, L. D.
    Lei, W. J.
    Chen, B. J.
    [J]. 3RD INTERNATIONAL PHOTONICS AND OPTOELECTRONICS MEETINGS (POEM 2010), 2011, 276
  • [10] Balling phenomena during direct laser sintering of multi-component Cu-based metal powder
    Gu, Dongdong
    Shen, Yifu
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 432 (1-2) : 163 - 166