Effect of Different V2O5 Salt Concentrations in Presence of Chloride and Sulfate Salt on Hot Corrosion Behavior of Functionally Graded Lanthanum Zirconate Thermal Barrier Coating

被引：0
|
作者：
Arpit R. Patil
S. T. Vagge
机构：
[1] Rajiv Gandhi Science and Technology Commission,
[2] Department of Metallurgy and Materials Science,undefined
[3] COEP Technological University,undefined
来源：
Protection of Metals and Physical Chemistry of Surfaces | 2023年 / 59卷
关键词：
LZ; multilayer FG TBC; hot corrosion; corrosive environment; vanadium;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：679 / 693
页数：14
相关论文
共 50 条
  • [1] Effect of Different V2O5 Salt Concentrations in Presence of Chloride and Sulfate Salt on Hot Corrosion Behavior of Functionally Graded Lanthanum Zirconate Thermal Barrier Coating
    Patil, Arpit R.
    Vagge, S. T.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2023, 59 (4) : 679 - 693
  • [2] Hot corrosion behaviour of plasma-sprayed functionally graded thermal barrier coatings in the presence of Na2SO4 + V2O5 molten salt
    Vakilifard, Hamide
    Ghasemi, Reza
    Rahimipour, Mohammadreza
    SURFACE & COATINGS TECHNOLOGY, 2017, 326 : 238 - 246
  • [3] Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4 + V2O5 or V2O5 salt at 900 °C
    Wang, Xizhong
    Guo, Lei
    Peng, Hui
    Zheng, Lei
    Guo, Hongbo
    Gong, Shengkai
    CERAMICS INTERNATIONAL, 2015, 41 (05) : 6604 - 6609
  • [4] Hot Corrosion of Iron in the Presence of Salt Mixture Deposit Containing NaCl and V2O5 at 600℃
    Lingchuan LI (Dept. of Materials Science and Engineering
    Journal of Materials Science & Technology, 1996, (06) : 445 - 451
  • [5] Hot-Corrosion Behavior of Gd2O3-Yb2O3 Co-Doped YSZ Thermal Barrier Coatings in the Presence of V2O5 Molten Salt
    Li, Yang
    She, Yajuan
    Liao, Kai
    COATINGS, 2023, 13 (05)
  • [6] Hot corrosion behavior of Sc2O3-Y2O3-ZrO2 thermal barrier coatings in presence of Na2SO4 + V2O5 molten salt
    Liu, Huai-fei
    Xiong, Xiang
    Li, Xiao-bin
    Wang, Ya-lei
    CORROSION SCIENCE, 2014, 85 : 87 - 93
  • [7] Hot corrosion behavior of multicomponent rare earth phosphate materials exposed to molten V2O5 salt
    Li, Lizhen
    Sun, Junbin
    Lu, Weihong
    Xu, Zhifeng
    CERAMICS INTERNATIONAL, 2024, 50 (17) : 31650 - 31664
  • [8] Hot corrosion of iron in the presence of salt mixture deposit containing NaCl and V2O5 at 600 degrees C
    Li, LC
    Zhu, RZ
    Gesmundo, F
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 1996, 12 (06) : 445 - 451
  • [9] Hot Corrosion Behavior of Inconel 625 in Na2SO4 and V2O5 Molten Salt System
    Li, Liang
    Li, Lanfeng
    Zhang, Guofeng
    Xue, Hongdi
    Cui, Maomao
    Wang, Wenxu
    Liu, Dexue
    METALS, 2023, 13 (06)
  • [10] Hot corrosion behavior of nanostructured Gd2O3 doped YSZ thermal barrier coating in presence of Na2SO4 + V2O5 molten salts
    Wang, Yixiong
    Zhou, Chungen
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2017, 27 (04) : 507 - 513
12345