Magnetic and electrical properties of lithium borosilicate glasses containing nickel and iron oxides

Measurements of a.c. conductivity, dielectric constants, Mo¨ssbauer spectra and magnetic susceptibility were carried out on samples of composition: 20LiO2, 31B2O5, 34SiO2, 15 − x NiO, xFe2O3 where x = 2.5, 5, 7.5, 10 and 12.5 mol %. It was found that when x is changed from 2.5 to 10 mol % NiO, the conductivity decreases due to the increase of the bridging oxygen ions. When x is increased to greater than 10 mol % NiO, the conductivity increases because of the decrease of the ratio of Fe2+Fe3+ ions as confirmed from Mo¨ssbauer data. The conductivity has a distinct minimum at 10 mol % NiO. Distribution of relaxation processes was also studied, and two processes were adequate to describe the present experimental data.