Antimicrobial polyurethane synthetic leather coating with In-situ generated Nano-TiO2

By incorporating organic-inorganic nano-hybridization into wet phase inversion coating-forming method, a novel antimicrobial polyurethane synthetic leather coating with in-situ generated nano-TiO2 (PUT) was prepared. The antibacterial activity against Staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa, Micrococcus luteus, antifungal activity against Aspergillus niger and toxicity of this PUT coating were investigated respectively. Experimental results showed that the antimicrobial activity of the PUT coating increased with increasing nano-TiO2 concentration. Low nano-TiO2 concentration (≤0.50 wt%) resulted in negligible or limited antimicrobial activity. When the nano-TiO2 concentration increased up to 0.75 and 1.00 wt%, the antibacterial activity of the PUT coating exceeded 82 and 93 % respectively, and no Aspergillus niger growth was observed on the coating surface within 28 days. Cell culture assay indicated that the PUT coating had no detrimental effect on the morphologies and proliferation rate of normal human dermal fibroblasts, which indicated a non-toxic and skin-friendly characteristic. According to these results, the PUT coating was capable of reducing the risk of microbial contamination while remained skin-friendly to wearers. More importantly, the organic-inorganic nano-hybridization technique developed in this study was carried out simultaneously during the established wet phase inversion coating-forming method for PU leather manufacture, which promised its possible application on an industrial scale.