Preparation of cellulose diacetate/cellulose hybrid fiber by dry-jet wet spinning in tetrabutylammonium acetate/dimethyl sulfoxide solvent

Cellulose diacetate (CDA)/cellulose hybrid fibers with nice properties were prepared by dry-jet wet spinning using a tetrabutylammonium acetate/dimethylsulfoxide system as a solvent at 50 °C. Scanning electron microscopy (SEM) images exhibited the hybrid fibers with circular cross section and smooth surface. In addition, SEM and Fourier transform infrared spectroscopy analysis indicated the nice compatibility of CDA and cellulose. The hybrid fibers with the addition of CDA showed higher thermal stability and a wider range of degradation than pure cellulose material. It was found that the elongation at break of the fibers increased from 4.87 to 13.22% with increasing CDA/cellulose ratio from 0 to 4:6, which was comparable with CDA fiber spun from 1-butyl-3-methylimidazolium chloride. The 1095.5/cm Raman characteristic band of the hybrid fibers with lower intensity was observed, while it did not towards a higher wave number compared to that of fibers containing less CDA. In addition, the shear viscosity of the solutions exhibited a character of typical shear-thinning behaviour with variation of shear rates.