Investigation into Oxygen-Enriched Bottom-Blown Stibnite and Direct Reduction

The direct oxidation of stibnite (Sb2S3) using a gas mixture of nitrogen-oxygen was investigated in a pilot plant. Steady-state pilot operation of 5 and 10 t/d was normally observed during the pilot test of 100 days, and a cleaning experiment of high-antimony molten slag from oxygen-enriched bottom-blown was tested by direct reduction in a laboratory-scale electric furnace. Autogenous smelting was achieved without adding any other fuel, which guaranteed the feasibility and advantage of oxygen-enriched bottom-blown stibnite. Through analysis and calculation, the sulfur dioxide concentration in offgas was more than 8 pct, which meets the requirement for the preparation of sulfuric acid. In the reduction experiment, the effects of added CaO, the ratio of coal (ω = actual weight of coal/theoretical weight of coal), and the slag type on the reduction procedure were considered. The residual slag obtained after reduction averaged less than 1 g/ton Au and less than 1 wt pct Sb. The metal phase contained iron less than 3 wt pct, and the recoveries of Au in the metal phase were more than 98 pct. This process shows significant environmental and economic benefits compared with previous processes.