Direct electrodeposition of highly ordered gold nanotube arrays for use in non-enzymatic amperometric sensing of glucose

The authors describe vertically aligned gold nanotube arrays (Au-NTAs) and gold nanowire arrays (Au-NWAs) that were directly grown in alumina oxide templates by galvanostatic deposition. The morphology of the gold arrays can be controlled by adjusting the pH value of the plating bath. Scanning electron microscopy shows the nanoarrays to be highly ordered (with an average length of around 2 μm), and the opening width of the gold nanotube arrays to be uniform (with diameters of around 50 nm). The electrocatalytic activities of the Au-NTAs and Au-NWAs deposited on a glassy carbon electrode toward glucose oxidation were compared by cyclic voltammetry and amperometry at pH 7.2. The Au-NTAs yield higher amperometric currents. The respective glucose sensor, when operated at a working potential of 0.25 V (vs. SCE), exhibits a linear range that extends from 5 μM to 16.4 mM concentrations of glucose, a sensitivity of 44.2 μA mM−1 cm−2, and a detection limit of 2.1 μM (at an S/N ratio of 3). The excellent sensing performance is attributed to the large surface area and the fast electron transfer rate for the one-dimensional gold nanoarrays.