PMMA/organomodified montmorillonite nanocomposites prepared by in situ bulk polymerizationStudy of the reaction kinetics

Kinetics of the in situ bulk polymerization of methyl methacrylate in the presence of organomodified montmorillonite (MMT) was investigated using differential scanning calorimetry (DSC) and gravimetrically. Different amount and types of MMT under the trade names Cloisite were employed. Using DSC, the amount of heat released versus time, under isothermal conditions, was recorded, and eventually, the time evolution of polymerization rate and monomer conversion was calculated. Results on the variation of monomer conversion with reaction time were in good agreement to corresponding from the gravimetric measurements. The nanocomposites prepared were characterized with WAXD, TEM and FTIR, and their glass transition temperature, Tg, was measured with DSC. Depending on the added amount of nano-MMT, either exfoliated or intercalated structures were obtained. An enhancement of the polymerization rate with the presence of the nanoparticles was observed especially in the gel effect region. This was accompanied by a higher Tg and average molecular weight, as measured by GPC, of all nanocomposites compared to neat PMMA.