pH-metric study of the setting reaction of monocalcium phosphate monohydrate/calcium oxide-based cements

Hydraulic calcium phosphate cements (CPCs) that are used as osseous substitutes, set by an acid–base reaction between an acid calcium phosphate and a basic calcium salt (often a phosphate). In order to gain a better understanding of the setting of the monocalcium phosphate monohydrate–calcium oxide cement that we developed and in the aim to improve its mechanical properties, the setting reaction was studied by pH-metry. The two methods described in the literature were used. In the first, cement samples were prepared then crushed after different storage periods at 37 °C, 100% RH. The powder was then immersed in pure water with stirring and the pH was measured after equilibration. In the second technique, the starting materials were poured into water while stirring and the pH were followed over time. The two methods gave different results. The first procedure provided information concerning the pH of the surrounding liquid following the partial dissolution of the cement components, rather than any information about pH changes during setting. The second method is more appropriate to follow the pH variations during setting. In this second procedure, the effects of different parameters such as crushing time, stirring rate, liquid-to-powder (L/P) ratio and temperature were investigated. These parameters may impact substantially on the shape and position of the pH=f(t) curves. One or three pH jumps were observed during the setting depending on the composition of the liquid phase. The time at which these pH jumps occurred depended on the pH of the liquid phase, the concentration of the buffer, the crushing of starting materials, the L/P ratio and the temperature. Good linear correlations were obtained (i) between the time of the pH jumps and the L/P ratio and the temperature and (ii) between the time of the first pH jump and the compressive strength and the final setting time of the cements prepared with different liquid phases. It may be assumed in view of these correlations that the results obtained in dilute solution may be extrapolated to the conditions of cement sample preparation and that the mechanical properties of the cement are directly related to the phenomena that occur at the first pH jump which corresponds to precipitation of dicalcium phosphate dihydrate.