Comparison of equivalent oxide thickness and electrical properties of atomic layer deposited hafnium zirconate dielectrics with thermal or decoupled plasma nitridation process

The NH3 thermal annealing and decoupled plasma nitridation (DPN) processes are compared for the equivalent oxide thickness (EOT) scaling of atomic-layer-deposited hafnium zirconate (HfZrO2) gate dielectric. Detailed physical, optical, and electrical characteristics of nitrided HfZrO2 (HfZrON) film are reported. It is found that DPN can yield a thinner SiOx interfacial layer (IL) (about 0.12 nm more in terms of EOT scaling) and a more densified HfZrO2 layer compared to those obtained using NH3 thermal annealing at a 16% nitrogen dose. NH3 thermal nitridation causes a large nitrogen distribution tail at the SiOx IL/Si substrate interface and increases leakage current, which suppresses EOT scalability.