Development of refractory composite materials for glass production

被引：0
|
作者：
N. N. Shcherbakova
G. S. Rossikhina
L. L. Chernina
P. K. Zheltov
M. V. Ivanova
机构：
[1] Saratov Institute of Glass,
[2] Semiluki Refractory Works,undefined
[3] Saratov State Technical University,undefined
来源：
Glass and Ceramics | 2006年 / 63卷
关键词：
Compressive Strength; Composite Material; Service Testing; Concrete Sample; High Compressive Strength;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The Semiluki Refractory Works produces refractories according to the technology of concrete and keeps developing compositions and refining the technology for producing large-size products by vibromolding. The Saratov Institute of Glass has performed service testing of concrete samples and determined their physicomechanical characteristics. The testing of samples fired at temperatures not higher than 1000°C has demonstrated their rather high compressive strength (from 40 to 60 N/mm2).
引用
收藏
页码：17 / 19
页数：2
相关论文
共 50 条
  • [1] Development of refractory composite materials for glass production
    Shcherbakova, NN
    Rossikhina, GS
    Chernina, LL
    Zheltov, PK
    Ivanova, MV
    [J]. GLASS AND CERAMICS, 2006, 63 (1-2) : 17 - 19
  • [2] Thermophysical characteristics of refractory composite materials for glass production
    G. S. Rossikhina
    M. P. Shchedrin
    N. N. Shcherbakova
    [J]. Glass and Ceramics, 2008, 65 : 162 - 164
  • [3] THERMOPHYSICAL CHARACTERISTICS OF REFRACTORY COMPOSITE MATERIALS FOR GLASS PRODUCTION
    Rossikhina, G. S.
    Shchedrin, M. P.
    Shcherbakova, N. N.
    [J]. GLASS AND CERAMICS, 2008, 65 (5-6) : 162 - 164
  • [4] Basic trends in development of production of refractory materials for the glass industry in Russia
    Shchedrin, M. P.
    Shcherbakova, N. N.
    Murzin, I. V.
    [J]. GLASS AND CERAMICS, 2006, 63 (9-10) : 342 - 345
  • [5] Basic trends in development of production of refractory materials for the glass industry in Russia
    M. P. Shchedrin
    N. N. Shcherbakova
    I. V. Murzin
    [J]. Glass and Ceramics, 2006, 63 : 342 - 345
  • [6] Thermal conductivity of refractory materials used in the glass production industry
    Wang, H
    Wereszczak, AA
    [J]. THERMAL CONDUCTIVITY 25: THERMAL EXPANSION 13, 2000, 25 : 350 - 357
  • [7] Guidelines for development and production of composite materials
    Oborin, L.A.
    Statsura, V.V.
    Cherepanov, A.I.
    [J]. Khimicheskie Volokna, 2003, (03): : 38 - 43
  • [8] A technology for production of composite refractory materials for the lining of steel ladles
    Kochubeev, YN
    Kungurtsev, VN
    Mironova, LV
    Neklyudova, YV
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2005, 46 (02) : 81 - 84
  • [9] A Technology for Production of Composite Refractory Materials for the Lining of Steel Ladles
    Yu. N. Kochubeev
    V. N. Kungurtsev
    L. V. Mironova
    Yu. V. Neklyudova
    [J]. Refractories and Industrial Ceramics, 2005, 46 : 81 - 84
  • [10] Prospects for the development of refractory materials production in the Republic of Uzbekistan
    Adylov, GT
    Voronov, GV
    Kulagina, NA
    Mansurova, ÉP
    Riskiev, TT
    Rumi, MK
    Faiziev, SA
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2002, 43 (7-8) : 265 - 268
12345