Submicron diameter nickel filaments and their polymer-matrix composites

被引：0
|
作者：
Xiaoping Shui
D. D. L. Chung
机构：
[1] State University of New York at Buffalo,Composite Materials Research Laboratory
来源：
Journal of Materials Science | 2000年 / 35卷
关键词：
Polymer; Grain Size; Reflection; Nickel; Sulfone;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Discontinuous nickel filaments of diameter 0.4 μm and having a carbon core of diameter 0.1 μm were fabricated by electroplating nickel on discontinuous carbon filaments. They exhibited a grain size of 0.016 μm and electrical resistivity of about 5 × 10−6 Ω·cm. In an amount as low as 7 vol.% in a polymer (polyether sulfone) matrix, they resulted in a composite exhibiting electromagnetic interference shielding effectiveness of 87 dB and reflection coefficient 0.95 at 1–2 GHz, tensile strength 52 MPa, tensile ductility 1.0%, and density 1.87 g/cm3.
引用
收藏
页码：1773 / 1785
页数：12
相关论文
共 50 条
  • [1] Submicron diameter nickel filaments and their polymer-matrix composites
    Shui, XP
    Chung, DDL
    JOURNAL OF MATERIALS SCIENCE, 2000, 35 (07) : 1773 - 1785
  • [2] Use of submicron diameter carbon filaments for reinforcement between continuous carbon fiber layers in a polymer-matrix composite
    State Univ of New York at Buffalo, Buffalo, United States
    Carbon, 11 (1627-1631):
  • [3] Discontinuous surface-treated submicron-diameter carbon filaments as an interlaminar filler in carbon fiber polymer-matrix composites for vibration reduction
    Segiet, M
    Chung, DDL
    COMPOSITE INTERFACES, 2000, 7 (04) : 257 - 275
  • [4] USE OF SUBMICRON DIAMETER CARBON FILAMENTS FOR REINFORCEMENT BETWEEN CONTINUOUS CARBON-FIBER LAYERS IN A POLYMER-MATRIX COMPOSITE
    HUDNUT, SW
    CHUNG, DDL
    CARBON, 1995, 33 (11) : 1627 - 1631
  • [5] Magnetic properties of nickel filament polymer-matrix composites
    Shui, XP
    Chung, DDL
    JOURNAL OF ELECTRONIC MATERIALS, 1996, 25 (06) : 930 - 934
  • [6] POLYMER-MATRIX COMPOSITES
    REINHART, TJ
    ADVANCED MATERIALS & PROCESSES, 1990, 137 (01): : 33 - &
  • [7] Nanoparticles in polymer-matrix composites
    Sabine Schlabach
    Rolf Ochs
    Thomas Hanemann
    Dorothée Vinga Szabó
    Microsystem Technologies, 2011, 17 : 183 - 193
  • [8] Polymer-matrix composites for microelectronics
    Chung, DDL
    POLYMERS & POLYMER COMPOSITES, 2000, 8 (04): : 219 - 229
  • [9] Nanoparticles in polymer-matrix composites
    Schlabach, Sabine
    Ochs, Rolf
    Hanemann, Thomas
    Szabo, Dorothee Vinga
    MICROSYSTEM TECHNOLOGIES-MICRO-AND NANOSYSTEMS-INFORMATION STORAGE AND PROCESSING SYSTEMS, 2011, 17 (02): : 183 - 193
  • [10] Tribological behavior of polymer-matrix composites
    Feulner, Von R.
    Künkel, R.
    Kobes, M.O.
    Ehrenstein, G.W.
    Tribologie und Schmierungstechnik, 2009, 56 (03): : 11 - 17
12345