Effect of Tempering and Strain on Decomposition of Metastable Austenite in X210CrW12 Thixo-Cast Steel

Thixoforming of hot rolled X210CrW12tool steel led to the formation of globular austenitic grains (82.4 vol.%) surrounded by eutectic mixture (α-Fe and M7C3 carbides). The thixo-cast steel reached compression strength 4.8 GPa at plastic strain 34%. The analysis of pole figures after deformation indicated distinct texturization of microstructure in comparison with undeformed steel. Main texture components for austenite were {101}, 〈010〉, while ferrite did not reveal clearly formed orientation. DSC analysis confirmed that austenitic structure in the X210CrW12 steel was metastable and temperature of decomposition depended on the strain applied at 634 °C for the un-deformed sample and at 599 °C for sample compressed up to 4.8 GPa. Discontinuous transformation of austenite into perlite, that started mainly at grain boundaries and proceeded to the center, was the predominant mechanism responsible for the decomposition of globular grains in thixoformed X210CrW12 steel. The decomposition caused by tempering of supersaturated and severely strained steel led to obtaining characteristic product of transformation of higher hardness in comparison with only tempered sample. In the deformed sample the reaction started on slip bands and twins which revealed high density of defects, promoting precipitation of carbides, followed by local depletion in carbon as a result of α′- Fe formation. In contrast to non-deformed state they covered the area of grains. Two fronts of reaction α-Fe plate +M3C → mixture of α-Fe and M7C3 carbides were also observed.