Procedure and Setup for the Investigation of Composite Materials in Torsion at Temperatures up to 3300 K

被引：3
|
作者：
V. S Dzyuba
S. V. Oksiyuk
机构：
[1] National Academy of Sciences of Ukraine,Pisarenko Institute of Problem of Strength
来源：
Strength of Materials | 2003年 / 35卷 / 3期
关键词：
composite materials; torsion; uniform temperature field; heating of specimen; thermocouples;
D O I：
10.1023/A:1024677108800
中图分类号：
学科分类号：
摘要：
A procedure and a setup are proposed for the investigation of strength properties of composite materials under torsion at temperatures of up to 3300 K in vacuum and in an oxidizing or inert medium. The setup is fitted with a system for the program heating of specimens to realize conditions that are close to the working conditions of the material. This makes it possible to carry out tests at a heating rate of about 500 deg/s with a uniform temperature field maintained along the specimen length.
引用
收藏
页码：322 / 325
页数：3
相关论文
共 32 条
  • [1] METHODOLOGY AND RESULTS OF AN INVESTIGATION INTO THE STRENGTH OF COMPOSITE MATERIALS IN TORSION AT HIGH TEMPERATURES (TO 3300 K)
    Dzyuba, V. S.
    Kravchuk, L. V.
    Kuriat, R. I.
    Oksiyuk, S. V.
    Tokarskii, V. A.
    [J]. MECHANICS OF COMPOSITE MATERIALS, 2011, 47 (02) : 233 - 238
  • [2] Methodology and results of an investigation into the strength of composite materials in torsion at high temperatures (to 3300 K)
    V. S. Dzyuba
    L. V. Kravchuk
    R. I. Kuriat
    S. V. Oksiyuk
    V. A. Tokarskii
    [J]. Mechanics of Composite Materials, 2011, 47 : 233 - 238
  • [3] A setup for studying the strength and life of composite materials under program thermal and mechanical loading at temperatures up to 3300 K
    Dzyuba V.S.
    Oksiyuk S.V.
    [J]. Strength of Materials, 2004, 36 (5) : 529 - 531
  • [4] Investigation of strength of carbon-Carbon composite materials at temperatures from 293 to 3300 K under high-rate heating
    Dzyuba V.S.
    Oksiyuk S.V.
    [J]. Strength of Materials, 2005, 37 (1) : 99 - 104
  • [5] Theoretical investigation of structural and thermo-mechanical properties of thoria up to 3300 K temperature
    Szpunar, B.
    Szpunar, J. A.
    [J]. SOLID STATE SCIENCES, 2014, 36 : 35 - 40
  • [6] Sorption of nitrogen and argon on fibrous and composite materials at pressures up to 50 MPa and temperatures 347, 373, and 393 K
    Pribylov, AA
    Pribylov, AA
    Kardash, MM
    [J]. RUSSIAN JOURNAL OF PHYSICAL CHEMISTRY, 2005, 79 (07): : 1131 - 1135
  • [7] Investigation of fracture behavior of typical refractory materials up to service temperatures
    Brochen, Erwan
    Dannert, Christian
    Paul, Juliane
    Krause, Olaf
    [J]. Unified International Technical Conference on Refractories, UNITECR 2022 - Proceedings, 2022,
  • [8] A setup for studying the Seebeck effect in thick-film resistive materials at temperatures of 77-700 K
    Buts, VP
    Nedorezov, VG
    [J]. INSTRUMENTS AND EXPERIMENTAL TECHNIQUES, 1999, 42 (01) : 125 - 126
  • [9] Investigation on the Reduction Behavior of Coal Composite Pellet at Temperatures between 1373 and 1573 K
    Park, Hyunsik
    Sohn, Il
    Freislich, Michiel
    Sahajwalla, Veena
    [J]. STEEL RESEARCH INTERNATIONAL, 2017, 88 (03)
  • [10] Experimental investigation of the density and surface tension of molten lithium at temperatures up to 1300 K
    K. A. Yakimovich
    A. G. Mozgovoi
    [J]. High Temperature, 2000, 38 : 657 - 659
1234