One-pot hydrothermal synthesis of rod-like FeOOH/reduced graphene oxide composites for supercapacitor

被引:0
|
作者
Tingting Xiao
Changling Yang
Yonggen Lu
Fanlong Zeng
机构
[1] Donghua University,College of Chemistry, Chemical Engineering and Biotechnology
[2] Donghua University,State Key Laboratory for Modification of Chemical Fibers and Polymer Materials
[3] Donghua University,College of Material Science and Engineering
关键词
Graphene Oxide; Specific Capacitance; Thermo Gravimetric Analysis; Nickel Foam; CH3COONa;
D O I
暂无
中图分类号
学科分类号
摘要
FeOOH/reduced graphene oxide (rGO) composites have been synthesized by a facile hydrothermal method. The morphology and structure of the obtained products were examined by scanning electron microscope, Raman, X-ray diffraction, thermo gravimetric analysis, and BET. The results show that the FeOOH nanorods were formed on graphene sheets by oxidation of graphene oxide rather than the O2 in air, and CH3COONa benefited the growth of FeOOH rods but is not necessary. The products were about 150 nm long obtained with the existence of CH3COONa, while 50 nm long without CH3COONa. The FeOOH/rGO generated with CH3COONa showed capacitance of 501.71 F/g at current density of 2 A/g in 1 mol/L NaOH, while that generated without CH3COONa showed higher specific capacitance of 537.14 F/g. The difference may be related to the amount of rGO, for the former one contained 82.61 wt% FeOOH while the later one contained 66.13 wt% FeOOH, which indicates the quantity of rGO and the their combination played an important role in the performance of the electrode materials.
引用
收藏
页码:3364 / 3374
页数:10
相关论文
共 50 条
  • [1] One-pot hydrothermal synthesis of rod-like FeOOH/reduced graphene oxide composites for supercapacitor
    Xiao, Tingting
    Yang, Changling
    Lu, Yonggen
    Zeng, Fanlong
    [J]. JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2014, 25 (08) : 3364 - 3374
  • [2] One-Pot Synthesis of Reduced Graphene Oxide/Metal (Oxide) Composites
    Wu, Xu
    Xing, Yugian
    Pierce, David
    Zhao, Julia Xiaojun
    [J]. ACS APPLIED MATERIALS & INTERFACES, 2017, 9 (43) : 37962 - 37971
  • [3] One-pot synthesis of ZnO/reduced graphene oxide nanocomposite for supercapacitor applications
    Bu, Ian Y. Y.
    Huang, Ray
    [J]. MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING, 2015, 31 : 131 - 138
  • [4] One-pot hydrothermal synthesis of reduced graphene oxide/carbon nanotube/α-Ni(OH)2 composites for high performance electrochemical supercapacitor
    Chen, Xi'an
    Chen, Xiaohua
    Zhang, Fengqiao
    Yang, Zhi
    Huang, Shaming
    [J]. JOURNAL OF POWER SOURCES, 2013, 243 : 555 - 561
  • [5] One-pot Hydrothermal Synthesis of Novel NiCoO2/Reduced Graphene Oxide Composites for Supercapacitors
    Wang Hongzhi
    Shi Xin
    Shi Yulei
    Zhang Weiguo
    Yao Suwei
    [J]. CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2017, 33 (04) : 638 - 642
  • [6] One-pot hydrothermal synthesis of novel NiCoO2/reduced graphene oxide composites for supercapacitors
    Hongzhi Wang
    Xin Shi
    Yulei Shi
    Weiguo Zhang
    Suwei Yao
    [J]. Chemical Research in Chinese Universities, 2017, 33 : 638 - 642
  • [7] One-pot hydrothermal synthesis of ZnS-reduced graphene oxide composites with enhanced photocatalytic properties
    Feng, Yan
    Feng, Ningning
    Zhang, Guoying
    Du, Guixiang
    [J]. CRYSTENGCOMM, 2014, 16 (02): : 214 - 222
  • [8] From graphite to interconnected reduced graphene oxide: one-pot synthesis and supercapacitor application
    Sidhureddy, Boopathi
    Thiruppathi, Antony Raj
    Chen, Aicheng
    [J]. CHEMICAL COMMUNICATIONS, 2017, 53 (55) : 7828 - 7831
  • [9] Reduced graphene oxide supported platinum nanocubes composites: one-pot hydrothermal synthesis and enhanced catalytic activity
    Li, Fumin
    Gao, Xueqing
    Xue, Qi
    Li, Shuni
    Chen, Yu
    Lee, Jong-Min
    [J]. NANOTECHNOLOGY, 2015, 26 (06)
  • [10] One-pot hydrothermal synthesis of ruthenium oxide nanodots on reduced graphene oxide sheets for supercapacitors
    Chen, Yao
    Zhang, Xiong
    Zhang, Dacheng
    Ma, Yanwei
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 511 (01) : 251 - 256