Indentation strength method to determine the fracture toughness of La0.58Sr0.4Co0.2Fe0.8O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ

被引:0
|
作者
B. X. Huang
A. Chanda
R. W. Steinbrech
J. Malzbender
机构
[1] Forschungszentrum Jülich GmbH,Mechanical Engineering Department
[2] Jadavpur University,undefined
来源
关键词
Residual Stress; Fracture Toughness; Perovskite; Domain Switching; Stable Crack Growth;
D O I
暂无
中图分类号
学科分类号
摘要
The temperature-dependent fracture toughness of brittle ceramics can be conveniently assessed from bending tests of specimens with defined cracks introduced by indentation. However, the validity of this indentation strength in bending method (ISM) depends critically on the correct consideration of the residual stress induced by the indentation process. The ISM has been applied to La0.58Sr0.4Co0.2Fe0.8O3-δ (LSCF) and, for comparison, on Ba0.5Sr0.5Co0.2Fe0.8O3-δ (BSCF) perovskite. LSCF with rhombohedral phase exhibits ferro-elastic behavior at ambient temperature, whereas BSCF deforms linear-elastically. Pre-indented specimens of both perovskites were fractured at room temperature in biaxial bending, some of them after an additional annealing step. The fracture toughness values of BSCF match reasonably well when determined with equations which consider the presence or absence of residual indentation stress. Interestingly, annealing has little influence on the apparent toughness results obtained for rhombohedral LSCF, which appears to be related with stress relaxation by ferro-elastic deformation.
引用
收藏
页码:2695 / 2699
页数:4
相关论文
共 50 条
  • [1] Indentation strength method to determine the fracture toughness of La0.58Sr0.4Co0.2Fe0.8O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ
    Huang, B. X.
    Chanda, A.
    Steinbrech, R. W.
    Malzbender, J.
    [J]. JOURNAL OF MATERIALS SCIENCE, 2012, 47 (06) : 2695 - 2699
  • [2] Transitions of Ba0.5Sr0.5Co0.8Fe0.2O3-δ and La0.58Sr0.4Co0.2Fe0.8O3-δ
    Araki, Wakako
    Arai, Yoshio
    Malzbender, Juergen
    [J]. MATERIALS LETTERS, 2014, 132 : 295 - 297
  • [3] Elastic anomaly and internal friction of Ba0.5Sr0.5Co0.8Fe0.2O3-δ and La0.58Sr0.4Co0.2Fe0.8O3-δ
    Huang, Bingxin
    Malzbender, Juergen
    Steinbrech, Rolf W.
    [J]. JOURNAL OF MATERIALS RESEARCH, 2011, 26 (11) : 1388 - 1391
  • [4] Elastic anomaly and internal friction of Ba0.5Sr0.5Co0.8Fe0.2O3-δ and La0.58Sr0.4Co0.2Fe0.8O3-δ
    Bingxin Huang
    Jürgen Malzbender
    Rolf W. Steinbrech
    [J]. Journal of Materials Research, 2011, 26 : 1388 - 1391
  • [5] Synthesis and characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ
    Ried, P.
    Holtappels, P.
    Wichser, A.
    Ulrich, A.
    Graule, T.
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2008, 155 (10) : B1029 - B1035
  • [6] Synthesis and characterization of Ba0.5Sr0.5Co0.8Fe0.2O3-σ
    Wang Qibao
    Yuan Yan
    Han Minfang
    Zhu Peiyu
    [J]. RARE METALS, 2009, 28 (01) : 39 - 42
  • [7] Ba0.5Sr0.5Co0.8Fe0.2O3-δ-La0.6Sr0.4Co0.8Fe0.2O3-δ COMPOSITE CATHODE FOR SOLID OXIDE FUEL CEL
    Mosialek, M.
    Kedra, A.
    Krzan, M.
    Bielanska, E.
    Tatko, M.
    [J]. ARCHIVES OF METALLURGY AND MATERIALS, 2016, 61 (03) : 1137 - 1141
  • [8] Synthesis and characterization of Ba0.5Sr0.5Co0.8Fe0.2O3-σ
    WANG Qibao
    [J]. Rare Metals, 2009, 28 (01) : 39 - 42
  • [9] Structure and oxygen stoichiometry of SrCo0.8Fe0.2O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ
    McIntosh, Steven
    Vente, Jaap F.
    Haije, Wim G.
    Blank, Dave H. A.
    Bouwmeester, Henny J. M.
    [J]. SOLID STATE IONICS, 2006, 177 (19-25) : 1737 - 1742
  • [10] Characterisation of La0.6Sr0.4CO0.2Fe0.8O3-δ - Ba0.5Sr0.5CO0.8Fe0.2O3-δ composite as cathode for solid oxide fuel cells
    Giuliano, Alice
    Carpanese, Maria Paola
    Panizza, Marco
    Cerisola, Giacomo
    Clematis, Davide
    Barbucci, Antonio
    [J]. ELECTROCHIMICA ACTA, 2017, 240 : 258 - 266