Study of ductile mode cutting in grooving of tungsten carbide with and without ultrasonic vibration assistance

In this study, ductile mode chip formation in conventional cutting and ultrasonic vibration assisted cutting of tungsten carbide workpiece material has been investigated through experimental grooving tests using CBN tools on a CNC lathe. The experimental results show that as the depth of cut was increased there was a transition from ductile mode to brittle mode chip formation in grooving both with and without ultrasonic vibration assistance. However, the critical value of the depth of cut for ductile mode cutting with ultrasonic vibration assistance was much larger than that without ultrasonic vibration assistance. The ratio of the volume of removed material to the volume of the machined groove, fab, was used to identify the ductile mode and brittle mode of chip formation in the grooving tests, in which fab<1 indicates ductile mode chip formation and fab>1 indicates brittle mode chip formation. For the same radius of tool cutting edge, the value of fab at the ductile-brittle transition region either with or without ultrasonic vibration was less than 1. However, the fab value with ultrasonic vibration assistance was close to 1. The experimental results demonstrate that ultrasonic vibration assisted cutting can be used to improve the ductile mode cutting performance of tungsten carbide work material.